Abstract:Single-phase Li0.5-0.5xZnxFe2.5-0.5xO4 (where x=0.0, 0.2, 0.3, 0.4, 0.5 and 0.8) nanofibers with diameters of 50 similar to 100 nm were successfully fabricated via electrospinning technique in combination with subsequent heat treatment using polyvinylpyrrolidone, nickel nitrate, zinc nitrate and ferric nitrate as principal raw material. The thermal decomposition process of as-spun precursor nanofibers and the influences of the calcination temperature and chemical composition on the crystal structure, micromorphology and magnetic properties of the prepared nanofiber samples were investigated by means of thermogravimetric and differential thermal analysis, X-ray diffraction, field emission scanning electron microscopy, transmission electron microscopy and vibrating sample magnetometer. The results indicate that the pure crystalline LiZn ferrite nanofibers are basically formed when the precursor nanofibers are calcined at 350 degrees C for 2 h. As the calcination temperature increases from 350 to 600 degrees C, the average grain size of Li0.35Zn0.3Fe2.35O4 nanofibers ranges from 13.0 to 47.5 nm and the micromorphology evolves toward a chain-like structrue. The saturation magnetization of the samples monotonously increases from 39.7 to 84.5 A.m(2).kg(-1), while the coercivity increases initially, reaches a maximun value of 12.6 kA.m(-1) at 550 C and then decreases, which reveals that the magnetic single-domain critical size of Li0.35Zn0.3Fe2.35O4 nanofibers may be around 35 nm. The lattice constant of as-prepared Li0.5-0.5xZnxFe2.5-0.5xO4 nanofibers calcined at 500 degrees C for 2 h exhibits an almost linear increase with increasing x and complies with Vegard's law. The coercivity of these nanofiber samples gradually decreases from 17.1 kA.m(-1) for x=0.0 to 2.4 kA.m(-1) for x=0.8, and the saturation magnetization firstly increases to 74.7 A.m(2).kg(-1) with the value of x up to 0.3 and then decreases beyond this limit. Compared to the nanoparticle counterparts prepared under similar conditions, the LiZn ferrite nanofibers have a relatively high coercivity due to their large shape anisotropy. These LiZn ferrite nanofibers have potential application in many fields such as nanoelectronic devices, sensitive devices, microwave absorbers, and biomedicine.

ZnFe2O4 Nanocrystals: Synthesis and Magnetic Properties

Synthesis of Nanocrystalline Ferrites Zn0.4ni0.6cr0.5laxfe1.5-Xo4 and Its Magnetic Properties

Synthesis of ZnFe 2 O 4 Nanomagnets by Fe-ion Implantation into ZnO and Post-Annealing

Synthesis and characterization of nanocrystallite ZnCrFeO4

ChemInform Abstract: High‐Yield Synthesis and Magnetic Properties of ZnFe2O4 Single Crystal Nanocubes in Aqueous Solution.

Effect of Zn Substitution on Morphology and Magnetic Properties of Cufe2o4 Nanofibers

Synthesis and Magnetic Properties of Single-Crystalline Magnetite Nanowires

High-temperature Solid State Synthesis and Characterization in Magnetic and Transporting Properties of Zn_xFe_(3-x)O_4 Powder

Magnetism of Zno Nanoparticles: Dependence on Crystallite Size and Surfactant Coating

Nanoarchitectonics of zinc nickel ferrites by the hydrothermal method for improved structural and magnetic properties

The Structure-Tunable Synthesis and Magnetic Properties of Fe3o4 Nanocrystals

Synthesis of CoFe2O4 Nanoparticles via Solution Method and Their Magnetic Properties

Superparamagnetic Nanoparticles Formed in Fe-implanted ZnO

Co-Precipitation Synthesis of ZNCF Nanoparticle and their Structure, Morphological, and Magnetic Properties Characterization

A Simple Solution Route to Control Synthesis of Fe3O4 Nanomaterials at Low Temperature and Their Magnetic Properties

Synthesis and Magnetic Properties of Mn-Zn Ferrite Nanoparticles

Synthesis and Magnetic Properties of Cobalt Ferrite (CoFe2O4) Nanoparticles Prepared by Wet Chemical Route

Synthesis of Nickel-Zinc Ferrite Nanoparticles by the Sol-Gel Auto-Combustion Method: Study of Crystal Structural, Cation Distribution, and Magnetic Properties

Transparent Magnetic Composites of ZnFe2O4 Nanoparticles in Silica

Facile hydrothermal synthesis of ZnCo2O4 nanostructures: controlled morphology and magnetic properties

Electrospinning Preparation, Structural and Magnetic Properties of Li0.5-0.5xznxfe2.5-0.5xo4 Nanofibers