Synthesis of CoFe2O4 Nanoparticles via Solution Method and Their Magnetic Properties

Tao PENG,Jianquan QI,Zhenxing YUE

DOI: https://doi.org/10.7521/j.issn.0454-5648.2013.05.23

2013-01-01

Abstract:CoFe2O4 nanoparticles were prepared by a direct synthesis method from solution using Co(NO3)2.6H2O and Fe(NO3)3 9H2O as raw materials.The phase structure,micro-morphology and synthesis mechanism of the nanoparticles were analyzed.The effect of annealing temperature on the magnetic properties of the samples was investigated.The results show that the products are cubic spinel-type ferrites with the average particle size of 5 nm,and the nanoparticles are well-dispersed.When the annealing temperature was < 500 ℃,the nanopraticles exhibited a superparamagnetic behavior.When the annealing temperature was > 500 ℃,the particle size,the specific saturation magnetization(Ms),the specific remnant magnetization(Mr) and the coercivity(Hc) of nanoparticles all increased with the increase of the annealing temperature.The Msof nanoparticles was 3.4 A.m2/kg at room temperature.When the annealing temperature was 900 ℃,theMsand the Hcfor the nanoparticles were 59.5 A.m2/kg and 97.0 kA/m,respectively.