Abstract:TiO2 nanocrystallines with a size of 3–7 nm have been synthesized by the sol–gel method with excessive water at a low temperature of about 50°C. The effects of amount of water and pH on the formation of sols and powders containing TiO2 nanocrystallines were investigated by X‐ray powder diffraction (XRD), transmission electron microscopy, and high‐resolution transmission electron microscopy. The results showed that a pure anatase phase was formed at pH 1, in contrast to the formation of particles with a mixture of anatase and brookite phases at pH 2–7. Moreover, at pH 1, the intensity of the XRD peaks and the crystal size increased with increasing water content when the water ratio increased from 40 to 100. Whereas the crystal intensity remained invariant, the crystal size still increased when the water ratio increased from 100 to 400. The photocatalytic activity was also investigated. It was shown that when the water ratio was below 100, the photocatalytic activity increased with increasing water content. Further increase of the water content decreased the photocatalytic activity. The photocatalytic activity decreased with increasing pH. All samples with pH=1 showed better photocatalytic activity than Degussa P25. Mechanisms for the formation of the TiO2 nanocrystalline particles at such a low temperature were also discussed.

TiO2–Ag Nanocomposites by Low‐Temperature Sol–Gel Processing

Low-Temperature Preparation of Ag-TiO2 Composite Films and Their Properties

Sol-Gel Preparation and Optical Properties of Ag Nanoparticle/TiO2 Composite Films

Improved Hydrogen Production by Glycerol Photoreforming over Ag2O-TiO2 Nanocomposite Mixed Oxide Synthesized by a Sol-gel Method

In-Situ Anatase Flake Crystals Prepared By Sol-Gel Method At Low Temperature

Synthesis of Ag/SiO2 nanocomposite material by adsorption phase nanoreactor technique

Preparation and Properties of TiO2/Bentonite Composite Photocatalytic Materials at Room Temperature

Effects of Heat-Treatment Temperature on Preparation of the Sol-Gel-Derived Ag/TiO2 Films

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature

Preparation and Properties of CaTiO_3:Zn Nanoparticles Based on Sol-Gel Method

Synthesis of MS/TiO2 (M = Pb, Zn, Cd) Nanocomposites Through a Mild Sol–gel Process

Study on the Preparation and Photocatalytic Properties of Au/TiO2 Composite Fibers

Sol-Gel Preparation of N-doped TiO2 Nanocrystalline at Low Temperature

Low temperature synthesis of visible light-driven vanadium doped titania photocatalyst

Preparation and Photocatalytic Activity of TiO<sub>2</sub>/Fe<sub>2</sub>O<sub>3 &Lt;/sub>nanocomposite

Preparation of Ti1-xFexO2 Nanocrystals via Low Temperature Sol-Gel Method

Formation of Ag Nanoparticles on Water-Soluble Anatase Tio2 Clusters and the Activation of Photocatalysis

Photocatalytic synthesis and photovoltaic application of Ag-TiO2 nanorod composites.

Synthesis of Ag/ZnO Nanocomposite with Excellent Photocatalytic Performance Via a Facile Sol-Gel Method

Novel Tio2-Pt@Sio2 Nanocomposites With High Photocatalytic Activity

Crystallization and Optical Behaviour of Nanocomposite Sol-Gel TiO2:Ag Films