Abstract:In this research, TiB2 powder was synthesized using the sol-gel process, resulting in nanometer-scale dimensions. Initially, a sol was prepared in a four-component system consisting of alcohol-dispersant-water-solvent.Various analytical techniques, including DLS, Zetameter, XRD, FTIR, SEM, and DTA/TG, were employed to elucidate the mechanism of product formation in the sol-gel process. Maintaining the pH within the range of 4 led to achieving TiB2 nanoparticles with precursors containing titanium and boron resources below 10 nm. The results of the viscosity and zeta potential tests showed that the solid particles in the sol are more stable in the pH range of less than 4 and have more favorable conditions to continue the synthesis process. FTIR data indicated the presence of B–Ti and carbon-containing bonds within the 600–1650 cm⁻1 range in the prepared gel powder. DTA analysis revealed that the initial nucleation of TiB2 particles occurred within the temperature range of 1300 °C. XRD patterns confirmed the formation of the TiB2 crystalline phase, which further progressed with increasing temperature, reaching up to 1400 °C. Surface analysis of the synthesized particles indicated a specific surface area of approximately 153.42 m2/g, with porous and meso-sized surfaces. Raman results showed the presence of Ti–B in the final product, and XPS graphs also confirmed these bonds. PSA results showed that the particle size distribution is in the range below 50 nm. SEM and TEM microstructural images provided visual evidence of the synthesis of TiB2 particles smaller than 100 nm, characterized by a narrow and uniform distribution range.

Al2O3/TiO2 core/shell powder derived by novel sol–gel routes

Sol–gel Synthesis and Sintering of Nano-Size Li2TiO3 Powder

The synthesis of nanosized TiO2 powder using a sol-gel method with TiCl4 as a precursor

The Microemulsion Method for Preparing TiO2 Coated SiO2 Core-Shell Particles

Electrical properties of TiO2/CO3O4 core/shell nanoparticles synthesized by sol-gel method

PREPARATION OF ANATASE TiO2 SOL AND POWDER BY SOLVOTHERMAL SYNTHESIS

Preparation and Characterization of TiB2/Al3Ti/Al2O3 Composite Nano-powder

Fabrication of Α-Alo(oh)·sio2 with Core-Shell Structures by Heterogeneous Nucleation-and-growth Processing

Preparation of Core–shell Nanostructured Black Nano-Tio2 by Sol–gel Method Combined with Mg Reduction

Liquid-phase deposition of TiO2 nanoparticles on core–shell Fe3O4@SiO2 spheres: preparation, characterization, and photocatalytic activity

Fabrication of tunable core-shell structured TiO2 mesoporous microspheres using linear polymer polyethylene glycol as templates

Preparation of Core/Shell Structure of α-Al(OH) 3 -SiO 2 by Heterogeneous Nucleation-and-Growth Processing

Highly Photocatalytic TiO 2 Interconnected Porous Powder Fabricated by Sponge-Templated Atomic Layer Deposition

Preparation of TiC/W Core–shell Structured Powders by One-Step Activation and Chemical Reduction Process

Single- and Mixed-Phase TiO2 Powders Prepared by Excess-Hydrolysis of a Titanium Alkoxide

Preparation of nanosized CoAl2O4 powders by sol–gel and sol–gel-hydrothermal methods

Mechanism Analysis and Preparation of Core-Shell Tio2/Sio2 Nanoparticles by H-2/Air Flame Combustions

Synthesis of Titanium Dioxide by Sol-Gel Method and Comparison with Titanium Dioxide Pure

Facile synthesis of fine Ti–Al intermetallic compound powders via sodiothermic reduction in molten CaCl2

Sol-gel synthesis and characterization of mesoporous TiB2 nano powder via Titanium isopropoxide /trimethyl borate precursors

Preparation of Nanocrystalline Anatase Tio2 Using Basic Sol-Gel Method