Abstract:The use of metal-coated ceramic powders not only effectively enhances the wettability of the metal–ceramic interface but also promotes a more uniform microstructure in Ti(C,N)-based cermets, which is advantageous for improving their mechanical properties. In this study, ultrafine Co- and Ni-coated (Ti,W,Mo,Ta)(C,N) powders were synthesized via the spray-drying-in-situ carbothermal reduction method. Subsequently, Ti(C,N)-based cermets were effectively fabricated using the as-prepared ultrafine Co- and Ni-coated (Ti,W,Mo,Ta)(C,N) powders. The impact of reaction temperature, heating rate, and isothermal time on the phase and microstructure of prepared powders was analyzed using X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). Additionally, the microstructure of the as-sintered cermets was experimentally investigated. The findings reveal that the complete reduction of Co and Ni metal salts, pre-coated on the surface of (Ti,W,Mo,Ta)(C,N) particles, can be achieved through rapid heating (10 °C/min) in a specific temperature range (600–1000 °C) with an isothermal time of 3 h at a lower reduction temperature (1000 °C). The synthesized powders have only two phases: the (Ti,W,Mo,Ta)(C,N) phase and Co/Ni phase, and no other heterogeneous phases were observed with an oxygen content of 0.261 wt.%. Notably, the conventional core–rim structure was not dominant in the cermets obtained from the prepared Co- and Ni-coated (Ti,W,Mo,Ta)(C,N) powders. Moreover, the heterogeneous segregation effect of the Co/Ni coating on the ultrafine powder particles resulted in a finer microstructure than the traditional cermets with the same composition. However, the grain size is mainly in the range of 0.5–0.8 μm. The weaker residual stresses at the core and rim interfaces and the finer particle distributions could theoretically enhance the toughness of Ti(C,N)-based cermets, simultaneously.

Preparation of TiC/W Core–shell Structured Powders by One-Step Activation and Chemical Reduction Process

Synthesis and Formation Mechanism of W/TiC Composite Powders by a Wet Chemical Route

Tungsten carbide (WC) nanopowders synthesized via novel core–shell structured precursors

In Situ Synthesis of Core-Shell W-Cu Nanopowders for Fabricating Full-Densified and Fine-Grained Alloys with Dramatically Improved Performance

Synthesis of nano (Ti,W)C powder with preferred orientation and twin boundary structure

Synthesis and characterization of multiwalled carbon nanotube/CdS core/shell heterostructures

Preparation and Characteristics of W–1 Wt.% TiC Alloy Via a Novel Chemical Method and Spark Plasma Sintering

Preparation and organization of W-Ni/TiC composite material

Preparation of Ultrafine Co- and Ni-Coated (Ti,W,Mo,Ta)(C,N) Powders and Their Influence on the Microstructure of Ti(C,N)-Based Cermets

A Versatile Kinetics-Controlled Coating Method to Construct Uniform Porous Tio2 Shells for Multifunctional Core-Shell Structures

Synthesis of WC-0.67wt.%Cr3C2 nanopowders by a one-step reduction-carbonization method and their characterization

Fabrication of Ultra-Fine-Grained W-TiC Alloys by a Simple Ball-Milling and Hydrogen Reduction Method

Al2O3/TiO2 core/shell powder derived by novel sol–gel routes

Synthesis and Electrochemical Performance of Novel Core/Shell Structured Nanocomposites

Stable nanoparticles dispersion induced an unprecedented high strength in a bulk W-TiC alloy

Preparation of core–shell PW<sub>12</sub>@TiO<sub>2</sub> microspheres and oxidative desulfurization performance

Singular tungsten disulfide core-shell and pure tungsten nanostructures

Study on influencing factors and mechanism of high-quality tungsten carbide nanopowders synthesized via carbothermal reduction

The Formation of Core–rim Structures in Fe40Al/(TiC–TiN–WC) Cermets Produced by Pressureless Melt Infiltration

Preparation and characterization of Au@TiO 2 core–shell hollow nanoparticles with CO oxidation performance

Preparation of core-shell PW 12 @TiO 2 microspheres and oxidative desulfurization performance.