Abstract:The titanium oxide (TiO 2 ) nanoparticles were synthesized through hydrolysis-condensation of Titanium (IV) n-butoxide [Ti(OBu n ) 4 ] by using a sol–gel-based hydrothermal method, also called the modified sol–gel method. In the synthesis of TiO 2 particles, the effect of water content and base types on the structure and surface properties of the particles was investigated. At the lowest water ratio ( r = 1, OTiO 2 -1), the formation of the anatase crystal phase was not complete, and at the water ratios above the stoichiometric ratio ( r = 25 and 50, OTiO 2 -25, and OTiO 2 -50), remains from the residual of the brookite phase. The crystallite sizes of OTiO2-1, OTiO 2 -2, OTiO 2 -4, OTiO 2 -10, OTiO 2 -25, and OTiO 2 -50 coded TiO 2 crystals that calculated by the Scherrer equation were 0,15 nm; 3.71 nm; 3.73 nm; 5.66 nm; 5.00 nm; 5,19 nm, respectively. In addition, transmission electron microscope (TEM) images of particles have been taken for comparison in order to confirm the calculated crystallite size from the Scherrer formula and obtained primary and secondary sizes from Zetasizer Nano. The optical absorption edge shifts to the higher energy region, that is, to a lower wavelength, with decreasing particle size. As it is expected, for OTiO 2 -2 and OTiO 2 -4, the absorption limits shifted to lower wavelength with decreasing crystallite size. The values of optical band gap energy confirm the crystal sizes obtained from the XRD analysis as it is associated with the reduction of crystallinity size, which determines the quantum size effect of the high bandgap. TiO 2 particles prepared using different bases were obtained in anatase form (except OTiO 2 -TMA), provided that the water ratio remains constant. The crystallite sizes of the particles were higher than those in an acidic medium, and the smallest OTiO 2 -NH 3 was obtained when their bases were compared to each other. When the absorption edges are examined according to the UV–Vis spectra, the red shift of the particles synthesized in the basic medium was more pronounced. While the band gap energies exhibited higher behavior in accordance with the size compared to the particles obtained in the acidic environment, it was determined that OTiO 2 -TMA had the highest band gap energy when compared with each other according to the base types. When SEM images were examined, spherical smooth particles were obtained as a result of using ammonia, which has less basic strength.

Synthesis of Titanium Dioxide by Sol-Gel Method and Comparison with Titanium Dioxide Pure

In-Situ Anatase Flake Crystals Prepared By Sol-Gel Method At Low Temperature

Synthesis and Characterization of High Surface Area Nano Titanium Dioxide

Synthesis of titanium dioxide nano-powder via sol–gel method at ambient temperature

Investigation on the Microstructure and Optical Performance of TiO_2 Films by Sol-Gel Method

Sol-Gel Preparation and Characterization of High Activity Titanium Dioxide Nanocrystalline Photocatalyst

Study of Titanium Dioxide Thin Film by Sol-Gel Method

Investigation of Mesoporous and Microporous Nanocrystalline Silicon-Doped Titania

Synthesis of Rutile and Anatase TiO2 Nanoparticles from Ti-peroxy Compound Aqueous Solution with Polyols

An investigation on the influence of hydrolysis ratio and base type on the characterization of synthesised nano-TiO2 by using sol–gel method

Sol-Gel Preparation and Optical Properties of Ag Nanoparticle/TiO2 Composite Films

pH control on preparation of nano-TiO_2 by gel-sol process

Characterization of TiO2 film prepared by sol-gel method using Ti(OC4H9)4

Preparation of Nanocrystalline Anatase Tio2 Using Basic Sol-Gel Method

Synthesis Of Nanocrystalline Tio2 By A Salt-Leaching Assisted Sol-Gel Method And Their Photoelectrochemical Properties

Studying of the structural and optical properties of titanium dioxide nanoparticles prepared by chemical method

Effect of Annealing Temperature on TiO2 Nanostructured Prepared by Sol-Gel Method

Sol–gel Synthesis of Macroporous TiO 2 from Ionic Precursors Via Phase Separation Route

Preparation of TiO_2 Nanoparticle and Their Photocatalytic Property

Sol-gel synthesis and characterization of mesoporous TiB2 nano powder via Titanium isopropoxide /trimethyl borate precursors

Fabrication and Optical Property Study of TiO2 Nanocrystalline Films by Sol-gel Methods