Abstract:TiO2 and TiO2-Al2O3 nanoparticles were synthesized via sol-gel method using hydrolysis of Titanium tetraisopropoxide (TTIP) with ethanol and water mixture as titania source. TiO2-Al2O3 Nano-composite was successfully synthesized using the sol-gel technique. Tetraisopropoxide and aluminium isopropoxide were used to prepare TiO2-Al2O3. All prepared samples calcination were conducted at different temperature (400 to 700) oC. The synthesized TiO2 and TiO2-Al2O3 nanocomposites were then characterized by XRD, AFM, BET surface area, SEM, XRF. XRD, the analysis showed that the presence of alumina (Al2O3) in the TiO2 has an effect on crystal size, particles size, surface area, and crystal phases; The XRD result revealed that the prepared TiO2 nanoparticles were anatase phase at 400oC, and 500oC, and transformed to rutile from 600oC to 700oC, but after addition of alumina TiO2 was of anatase phase, without any rutile at all calcination temperatures, also, the addition of alumina leads to a significant decrease in the crystal size, particles size, especially at high temperatures while the surface area of pure titanium was increased, and this corresponds to the results of the AFM and SEM. The best-obtained surface area was 355.18 m2/ gm. with 34.98 nm of average particle size at 500oC in comparison with pure nano titanium dioxide

Synthesis of titanium dioxide nano-powder via sol–gel method at ambient temperature

Preparation and Properties of TiO2/Bentonite Composite Photocatalytic Materials at Room Temperature

Synthesis of Titanium Dioxide by Sol-Gel Method and Comparison with Titanium Dioxide Pure

Effect of Calcination Temperature on Crystal Structure and Photocatalytic Prop- Erty of TiO2/Diatomite Nanoparticles

pH control on preparation of nano-TiO_2 by gel-sol process

Effect of drying environment on grain size of titanium dioxide nano-powder synthesized via sol-gel method

Preparation of Nanocrystalline Anatase Tio2 Using Basic Sol-Gel Method

Synthesis and Characterization of High Surface Area Nano Titanium Dioxide

Synthesis of Nanosized Rutile TiO2 Powder at Low Temperature

Synthesis of Size-Controlled Nanotitania Particles via a Simple Sol-Gel Method

The synthesis of nanosized TiO2 powder using a sol-gel method with TiCl4 as a precursor

Synthesis of Titanium Dioxide Nanobelts

Synthesis of Crystalline Nanosized Titanium Dioxide Via a Reverse Micelle Method at Room Temperature

Controlled Synthesis of Titanium Dioxide Nanostructures

Synthesis and Characterization of TiO2 Nano Powders by Pyrogenation-with-Sugar-Protection Method

Synthesis of Nano-TiO2 with Anatase Structure at Low Temperature

Synthesis of Nano-Sized SrTiO3 Photocatalyst by Sol-Gel Method

The Calcination Effect on the Crystallinity, Nitrogen Content, and Pore Structure of Nitrogen-Doped Titanium Dioxide

Effect of Annealing Temperature on TiO2 Nanostructured Prepared by Sol-Gel Method

Room Temperature Synthesis of Titania Microspheres by Hydrolysis of Titanium Alkoxide Using Water Vapor

Synthesis of Titanium-Based Powders from Titanium Oxy-Sulfate Using Ultrasonic Spray Pyrolysis Method