Abstract:TiO2 nanocrystallines with a size of 3–7 nm have been synthesized by the sol–gel method with excessive water at a low temperature of about 50°C. The effects of amount of water and pH on the formation of sols and powders containing TiO2 nanocrystallines were investigated by X‐ray powder diffraction (XRD), transmission electron microscopy, and high‐resolution transmission electron microscopy. The results showed that a pure anatase phase was formed at pH 1, in contrast to the formation of particles with a mixture of anatase and brookite phases at pH 2–7. Moreover, at pH 1, the intensity of the XRD peaks and the crystal size increased with increasing water content when the water ratio increased from 40 to 100. Whereas the crystal intensity remained invariant, the crystal size still increased when the water ratio increased from 100 to 400. The photocatalytic activity was also investigated. It was shown that when the water ratio was below 100, the photocatalytic activity increased with increasing water content. Further increase of the water content decreased the photocatalytic activity. The photocatalytic activity decreased with increasing pH. All samples with pH=1 showed better photocatalytic activity than Degussa P25. Mechanisms for the formation of the TiO2 nanocrystalline particles at such a low temperature were also discussed.

Synthesis of Nanosized Rutile TiO2 Powder at Low Temperature

Sol–gel Synthesis and Sintering of Nano-Size Li2TiO3 Powder

In-Situ Anatase Flake Crystals Prepared By Sol-Gel Method At Low Temperature

Synthesis of Nanocrystal Titania Sol with Different Ratio of Rutile and Anatase at Low Temperature

Sol-Gel Preparation of N-doped TiO2 Nanocrystalline at Low Temperature

Effect of hydrolysis conditions on morphology and crystallization of nanosized TiO2 powder

Low‐Temperature Growth of Monolayer Rutile TiO2 Nanorod Films

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature

A Novel Method for Preparation of Nanocrystalline Rutile TiO2 Powders by Liquid Hydrolysis of TiCl4

Synthesis of titanium dioxide nano-powder via sol–gel method at ambient temperature

Synthesis of Nano-TiO2 with Anatase Structure at Low Temperature

Synthesis of nanocrystalline rutile titania by Co-thermal hydrolysis of TiCl4 and TiCl3 solutions

Hydrothermal Preparation of Uniform Nanosize Rutile and Anatase Particles

Ni-doped Rutile TiO2 Nanoflowers: Low-Temperature Solution Synthesis and Enhanced Photocatalytic Efficiency

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

Low-temperature preparation of titania nanorods through direct oxidation of titanium with hydrogen peroxide

Low-temperature Synthesis of TiB2 Nanocrystals Using TiO2 ,LiBH4 and Mg

Synthesis of Rutile and Anatase TiO2 Nanoparticles from Ti-peroxy Compound Aqueous Solution with Polyols

Preparation of Nanocrystalline Anatase Tio2 Using Basic Sol-Gel Method

Preparation of nano-scale TiO2 with controllable rutile content by homogeneous hydrolysis

A New Method for Synthesizing Li2.06nb0.18ti0.76o3 Powder at Low Temperatures