Abstract:Nano-scaled pure and iron doping Titanium Dioxide prepared by TiCl4 hydrolysis were obtained. Two methods, step precipitation and co-precipitation, were applied in preparing the iron doping samples. The crystallization and decomposition processes were extensively investigated by methods of X-ray diffraction and TEM. The grain sizes under series of calcinating temperatures were computed according to Voigt function analysis. The results of TEM images also justified the computed grain size. The results showed that Titanium Dioxide prepared by TiCl4 hydrolysis is amorphous, and that no obvious: crystallization temperature or exothermic peaks were observed, contrary to the some previous reports. The computation applying the nuclei growth equation showed that the crystal grain growth of the pure and co-precipitation samples can be divided into 2 steps. The growth activation energy of the former step is 10.7kJ . mol(-1) and 8.6kJ . mol(-1), respectively and that of the latter step is 111.6kJ . mol(-1). As to the step precipitation samples, there showed no obvious difference in crystal growth activation energies for the 2 steps, and for the transformation of anantase to rutile was almost completed before 600 degrees C. There was evidence that the iron doping accelerated the transformation of rutile to anatase and this is especially obvious in step precipitation samples.

A Novel Method for Preparation of Nanocrystalline Rutile TiO2 Powders by Liquid Hydrolysis of TiCl4

The Thermal Analysis, Crystal Growth And Structure Transformation Of Nano-Scale Tio2 Prepared By Ticl4 Hydrolysis

Preparation and Photocatalytic Activities of TiO2 Nanotubes with Mixed Crystal Structure

Large-scale Synthesis and Characterization of Fan-Shaped Rutile TiO2 Nanostructures

In-Situ Anatase Flake Crystals Prepared By Sol-Gel Method At Low Temperature

Rapid-Heating-Triggered in Situ Solid-State Transformation of Amorphous TiO2 Nanotubes into Well-Defined Anatase Nanocrystals

Synthesis of Nanosized Rutile TiO2 Powder at Low Temperature

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

Hydrothermal Preparation of Uniform Nanosize Rutile and Anatase Particles

Direct Continuous Hydrothermal Synthesis of High Surface Area Nanosized Titania

Influence of solution concentration on the hydrothermal preparation of titania crystallites

Low-temperature preparation of titania nanorods through direct oxidation of titanium with hydrogen peroxide

Preparation of Single-Crystalline BaTi5O11 Nanocrystals by Hydrothermal Method

Synthesis and photocatalytic properties of nano bi-crystalline titania of anatase and brookite by hydrolyzing TiOCl2 aqueous solution at low temperatures

Preparation and Photocatalytic Activity of TiO<sub>2</sub>/Fe<sub>2</sub>O<sub>3 &Lt;/sub>nanocomposite

Synthesis of nanometer-sized TiO2 particles by a microemulsion method

Ordered Mesoporous Thin Films Of Rutile Tio2 Nanocrystals Mixed With Amorphous Ta2o5

Synthesis of Crystalline Nanosized Titanium Dioxide Via a Reverse Micelle Method at Room Temperature

Preparation of nanometer rutile TiO2 powder and its characteristics

Solvothermal Synthesis of Tio2: Anatase Nanocrystals and Rutile Nanofibres from Ticl4 in Acetone

Synthesis Of Crystal-Controlled Tio2 Nanorods By A Hydrothermal Method: Rutile And Brookite As Highly Active Photocatalysts