Abstract:In this article, we report a controllable and reproducible approach to prepare highly ordered 2-D hexagonal mesoporous crystalline TiO2-SiO2 nanocomposites with variable Ti/Si ratios (0 to infinity). XRD, TEM, and N2 sorption techniques have been used to systematically investigate the pore wall structure, and thermal stability functioned with the synthetic conditions. The resultant materials are ultra highly stable (over 900 degrees C), have large uniform pore diameters (approximately 6.8 nm), and have high Brunauer-Emmett-Teller specific surface areas (approximately 290 m2/g). These mesostructured TiO2-SiO2 composites were obtained using titanium isopropoxide (TIPO) and tetraethyl orthosilicate (TEOS) as precursors and triblock copolymer P123 as a template based on the solvent evaporation-induced co-self-assembly process under a large amount of HCl. Our strategy was the synchronous assembly of titanate and silicate oligomers with triblock copolymer P123 by finely tuning the relative humidity of the surrounding atmosphere and evaporation temperature according to the Ti/Si ratio. We added a large amount of acidity to lower condensation and polymerization rates of TIPO and accelerate the rates for TEOS molecules. TEM and XRD measurements clearly show that the titania is made of highly crystalline anatase nanoparticles, which are uniformly embedded in the pore walls to form the "bricked-mortar" frameworks. The amorphous silica acts as a glue linking the TiO2 nanocrystals and improves the thermal stability. As the silica contents increase, the thermal stability of the resulting mesoporous TiO2-SiO2 nanocomposites increases and the size of anatase nanocrystals decreases. Our results show that the unique composite frameworks make the mesostructures overwhelmingly stable; even with high Ti/Si ratios (> or =80/20) the stability of the composites is higher than 900 degrees C. The mesoporous TiO2-SiO2 nanocomposites exhibit excellent photocatalytic activities (which are higher than that for commercial catalyst P25) for the degradation of rhodamine B in aqueous suspension. The excellent photocatalytic activities are ascribed to the bifunctional effect of highly crystallized anatase nanoparticles and high porosity.

Room Temperature Synthesis of Titania Microspheres by Hydrolysis of Titanium Alkoxide Using Water Vapor

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

Hydrolysis of Titanium Alkoxide in Organic Solvent at High Temperatures: A New Synthetic Method for Nanosized, Thermally Stable Titanium(IV) Oxide

Template-free Hydrothermal Synthesis of Macroporous TiO2 Microspheres on a Large Scale

HYDROTHERMAL SYNTHESIS OF TITANIUM DIOXIDE NANOSTRUCTURAL HOLLOW SPHERES WITH HIGH PHASE TRANSITION TEMPERATURE

Direct Continuous Hydrothermal Synthesis of High Surface Area Nanosized Titania

Preparation and Characterization of Anatase TiO2 Microspheres with Porous Frameworks Via Controlled Hydrolysis of Titanium Alkoxide Followed by Hydrothermal Treatment

Effect of Calcination Temperature on Crystal Structure and Photocatalytic Prop- Erty of TiO2/Diatomite Nanoparticles

Synthesis of titanium dioxide nano-powder via sol–gel method at ambient temperature

Control of Microscopic Morphology and Structure of One Dimensional Titanium Dioxide Nanomaterials

A Simple Solution-Phase Route for Room-Temperature Synthesis of Mesoporous and Nanocrystalline Anatase Tio2

Preparation of Nanocrystalline Anatase Tio2 Using Basic Sol-Gel Method

Controllable and Repeatable Synthesis of Thermally Stable Anatase Nanocrystal-Silica Composites with Highly Ordered Hexagonal Mesostructures.

Controlling crystallinity of nano-titania powder prepared by the hydrolysis of titanium alkoxide

Synthesis and characterization of nanosized anatase TiO2 cuboids

Effect of hydrolysis conditions on morphology and crystallization of nanosized TiO2 powder

Synthesis of Nanocrystal Titania Sol with Different Ratio of Rutile and Anatase at Low Temperature

Synthesis of Spherical Titania by Hydrolysis Using Industrial Titanium Sulfate Solution

Morphology and Structure of Nanosized TiO2 Particles Synthesized by Gas-Phase Reaction

Preparation and Characterization of Nanosized Anatase TiO2 Cuboids for Photocatalysis

Low-Temperature Synthesis of Nanostructured TiO2 Particles and Their Photocatalytic Oxidation Activity