Abstract:Titanium dioxide (TiO2) has been extensively investigated as a photocatalyst for water splitting to produce H-2. However, an overall water splitting by using anatase TiO2 is extremely difficult due to the short lifetime of holes. In this work, we propose that a surface energy decrease from {001} to {101} of anatase TiO2 is able to drive an epitaxial growth. A novel anatase TiO2 homostructure has been successfully synthesized via a facile hydrothermal route, where {101} semi-pyramid nanoparticles epitaxially grew on the both sides of the {001} nanosheets. The epitaxial relationship between the nanoparticles and the nanosheets has been characterized to be {001}/1{001} of anatase TiO2. For the first time, it is interesting to find that the homostructure with 12 wt% of {101} semi-pyramid can significantly improve the H-2 evolution rate by nearly 5 times compared to the pure nanosheets under the ultraviolet irradiation. More importantly, such homostructure enables 10.78 mu mol g(-1) h(-1) of O-2 production whereas the pure nanosheets cannot evolve detectable O-2 gas. Meanwhile, the time-resolved photoluminescence analysis indicates that the mean lifetime of the holes is increased from 2.20 ns of the nanosheets to 3.59 ns of the homostructure, accounting for the observed overall water splitting. The findings suggest that constructing a homostructure by a surface energy strategy could be promising towards overall water splitting, which may be applicable to other photocatalytic materials. (C) 2020 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.

Hydrothermal growth of multi-facet anatase spheres

Hierarchical Spheres Assembled from Large Ultrathin Anatase TiO2 Nanosheets for Photocatalytic Hydrogen Evolution from Water Splitting

Hydrothermal Growth of Nanometer- to Micrometer-Size Anatase Single Crystals with Exposed (001) Facets and Their Ability to Assist Photodegradation of Rhodamine B in Water.

One-pot synthesis of N-F-Cr-doped anatase TiO₂ microspheres with nearly all-(001) surface for enhanced solar absorption.

Alkaline hydrothermal synthesis of homogeneous titania microspheres with urchin-like nanoarchitectures for dye effluent treatments.

Synthesis and Characterization of Anatase TiO2 Microspheres Self-Assembled by Ultrathin Nanosheets

Synthesis, Characterization and Photocatalytic Activity of Hierarchical Spherical TiO2 Nanostructures

Template-free Hydrothermal Synthesis of Macroporous TiO2 Microspheres on a Large Scale

Anatase TiO 2 hollow microspheres with exposed {0 0 1} facets: Facile synthesis and enhanced photocatalysis

A Simple Solvothermal Process to Synthesize CaTiO3 Microspheres and Its Photocatalytic Properties

Surface Defect-Controlled Growth and High Photocatalytic H-2 Production Efficiency of Anatase TiO2 Nanosheets

Surface Energy-Driven Solution Epitaxial Growth of Anatase TiO2 Homostructures for Overall Water Splitting

Hydrothermal synthesis of hydrangea-like F-doped titania microspheres for the photocatalytic degradation of carbamazepine under UV and visible light irradiation

Shape‐ and Size‐Controlled Synthesis of Uniform Anatase TiO2 Nanocuboids Enclosed by Active {100} and {001} Facets

A Novel Etching and Reconstruction Route to Ultrathin Porous TiO2 Hollow Spheres for Enhanced Photocatalytic Hydrogen Evolution

Facet-dependent Decoration of TiO2 Mesocrystals on TiO2 Microcrystals for Enhanced Photoactivity

Hollow TiO 2 microspheres assembled with rutile mesocrystals: Low-temperature one-pot synthesis and the photocatalytic performance

Synthesis and photo activity of flower-like anatase TiO2 with {001} facets exposed

Hydrothermal Synthesis, Characterization and Formation Mechanism of Self-Assembled Mesoporous SrTiO3 Spheres Assisted with Na2SiO3·9H2O

Simultaneous formation of silica-protected and N-doped TiO2 hollow spheres using organic–inorganic silica as self-removed templates

Self-assembly and Photocatalysis of Mesoporous TiO 2 Nanocrystal Clusters