Abstract:Well-crystallized anatase thin films with controlled thickness of 0.4–0.8μm were deposited on conductive titanium substrates through hydrolysis of titanium tetrafluoride aqueous solution at a low temperature of 60°C for various durations. A comparative study was carried out on their abilities to assist photocatalytic (PC) and photoelectrocatalytic (PEC) degradation of rhodamine B (RhB) in water. The efficiency of the anatase thin film to assist photodegradation of RhB improved significantly with an applied potential of 0.4V versus SCE, independence of the film thickness and the calcination temperature. The PC degradation rate increased linearly with increasing film thickness to ca. 0.54μm, which remained stable with further increasing film thickness. The PEC degradation rate increased dramatically with slightly increasing film thickness from 0.41 to 0.46μm, which then decreased with further increasing film thickness. After a subsequent calcination at 500°C, the PC degradation rate reached the optimum value because of the bargaining effect between the increasing crystallinity and increasing grain size with increasing calcination temperatures. The appearance of rutile phase after calcination at temperatures beyond 600°C due to the direct oxidation of the Ti substrate deteriorated additionally the photocatalytic activity. The optimum calcination temperature for the PEC degradation rate was 500–600°C due to the additional effect of increasing conductivity of the anatase film with the increasing calcination temperature.

Hydrothermal Growth of Nanometer- to Micrometer-Size Anatase Single Crystals with Exposed (001) Facets and Their Ability to Assist Photodegradation of Rhodamine B in Water.

Low-Temperature Deposition of Anatase Thin Films on Titanium Substrates and Their Abilities to Photodegrade Rhodamine B in Water

In-Suit Preparation of Cubic Anatase Tio2 Crystals and Its Photocatalysis Property on Rhodamine B

Hydrothermal growth of multi-facet anatase spheres

Surface Defect-Controlled Growth and High Photocatalytic H-2 Production Efficiency of Anatase TiO2 Nanosheets

Tuning the Photoelectronic and Photocatalytic Properties of Single-Crystalline TiO 2 Nanosheet Array Films with Dominant {001} Facets by Controlling the Hydrochloric Acid Concentration

Photocatalytic and photoelectrocatalytic degradation of aqueous Rhodamine B by low-temperature deposited anatase thin films

(001)-Exposed TiO2 Microcrystals Decorated with Few-Layer Nanobelts for Enhanced Photocatalytic Activity

Photodegradation Of Rhodamine B In Water Assisted By Titania Nanorod Thin Films Subjected To Various Thermal Treatments

One-pot synthesis of N-F-Cr-doped anatase TiO₂ microspheres with nearly all-(001) surface for enhanced solar absorption.

Low-Temperature Growth of a Nitrogen-Doped Titania Nanoflower Film and Its Ability to Assist Photodegradation of Rhodamine B in Water

Alkaline hydrothermal synthesis of homogeneous titania microspheres with urchin-like nanoarchitectures for dye effluent treatments.

Facet-dependent Decoration of TiO2 Mesocrystals on TiO2 Microcrystals for Enhanced Photoactivity

Anatase TiO 2 hollow microspheres with exposed {0 0 1} facets: Facile synthesis and enhanced photocatalysis

Synthesis of Anatase Tio2 Nanocrystals with Exposed {001} Facets

Low‐Temperature Transformation of Titania Thin Films from Amorphous Nanowires to Crystallized Nanoflowers for Heterogeneous Photocatalysis

Anatase Tio2 Films with Dominant {001} Facets Fabricated by Direct-Current Reactive Magnetron Sputtering at Room Temperature: Oxygen Defects and Enhanced Visible-Light Photocatalytic Behaviors

Photodegradation of Rhodamine B in Water Assisted by Titania Films Prepared Through a Novel Procedure

Direct Continuous Hydrothermal Synthesis of High Surface Area Nanosized Titania

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

Photocatalytic degradation of dyestuff wastewater under visible light irradiation using micron-sized mixed crystal TiO2 powders