Abstract:Natural porous mineral supported (TiO2/diatomite) photocatalyst was prepared via a modified sol–gel method using titanium (IV) butoxide (TBOT) and diatomite. The effect of TBOT dosage on adsorption capacity and photocatalytic activity for Rhodamine B (RhB) solution was investigated. The morphology and elemental distribution were determined by scanning electron microscopy with attached energy-dispersive X-ray detector. The porous and crystalline structures were characterized using nitrogen adsorption–desorption and X-ray diffraction techniques, respectively. The prepared TiO2/diatomite hybrid catalyst has shown relatively even porous structure and dispersion of TiO2 over the surface. This suggests that the diatomite matrix prevented the agglomeration of TiO2 particles. Initially, the surface area and pore volume of the hybrid catalyst were increased by adding TBOT then decreased for dosages higher than 1.0ml. The crystalline size of TiO2 immobilized on diatomite matrix by sol–gel method was around 20nm. When the experiments were carried out in the absence of diatomite, this value was increased to 33.73nm. The use of diatomite also promoted an increase of the transformation temperature of the crystalline phase anatase to rutile for the TiO2. The as-prepared TiO2/diatomite composite exhibited high photocatalytic activity (96.0% for 0.5h UV-light irradiation) for the degradation of RhB from wastewater as a result of its unique porous structure and optimum TiO2 loading. In addition, it can be easily separated from suspension and possess a good durability. This hybrid material holds great promise in the engineering field for the environmental remediation.

In-Suit Preparation of Cubic Anatase Tio2 Crystals and Its Photocatalysis Property on Rhodamine B

In-Situ Anatase Flake Crystals Prepared By Sol-Gel Method At Low Temperature

Photo Degradation on Rhodamine B for Anatase Tio2 Sol under Uv, Visible Light and Ir

Preparation and Analysis of Photocatalytic TiO2 Sol

Preparation and investigation of TiO2 Sol containing nanometer anatase crystalline grains

Hydrothermal Growth of Nanometer- to Micrometer-Size Anatase Single Crystals with Exposed (001) Facets and Their Ability to Assist Photodegradation of Rhodamine B in Water.

Synthesis of Natural Porous Minerals Supported Tio2 Nanoparticles and Their Photocatalytic Performance Towards Rhodamine B Degradation

Low-Temperature Deposition of Anatase Thin Films on Titanium Substrates and Their Abilities to Photodegrade Rhodamine B in Water

Photocatalytic degradation of dyestuff wastewater under visible light irradiation using micron-sized mixed crystal TiO2 powders

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

Preparation Of Tio2 Sol Containing Anatase-Rutile Mischcrystal Grains And Its Photocatalytic Activity

Crystallization of Anatase from Amorphous Titania in Hot Water and in Vitro Biomineralization.

Low-Temperature Preparation of Phthalocyanine-Sensitized Mischcrystal Tio2 Film and Its Catalysis for Degradation of Rhodamine B

Preparation and Investigation of TiO<sub>2</sub> Sol Containing Nanometer Anatase Crystalline Grains

Photocatalytic and photoelectrocatalytic degradation of aqueous Rhodamine B by low-temperature deposited anatase thin films

Synergistic Photosensitized Removal of Cr(VI) and Rhodamine B Dye on Amorphous TiO2 under Visible Light Irradiation.

Research on nanometer crystal anatase TiO2 sol excitated by broad range light spectrum

Solar photocatalytic degradation of dye wastewater in the presence of heat‐treated anatase TiO<sub>2</sub>powder

Effect of Water Amount on the Preparation, Structure and Property of Anatase Sol

Effect of Calcination Temperature on Crystal Structure and Photocatalytic Prop- Erty of TiO2/Diatomite Nanoparticles

Effect of sol concentration on photocatalytic reaction of anatase TiO2 sol