Abstract:Three-dimensional (3D) titania nanostructures assembled with ordered rutile nanorods have been fabricated via a surfactant-free and single-step solvothermal route. The effects of preparation parameters, including the reaction temperatures and the reactant concentrations, on the microstructure, optical properties and photocatalytic activity of the 3D TiO2 nanostructures were investigated. The results revealed that 3D TiO2 microspheres possessed a dandelion-like morphology composed of radially packed rutile nanorods. Increasing the reaction temperature leads to the formation of larger rutile crystals, but reduced the aspect ratios of nanorods. The morphology of products was dominated by irregular shapes with low titanium precursor concentration. The optical reflectance, absorption and photocatalytic properties of the samples were found to be significantly dependent on their morphology. 3D dandelion-like structures with tapered tips showed lower reflectance, more efficient light harvesting, higher surface area and consequently higher photocatalytic activity compared with those with flat tops and fragment of nanorod sectors. Moreover, TiO2 products prepared with 0.4M titanium precursor solution at 150 and 120°C showed better or equivalent photocatalytic activity compared with Degussa P25 owing to high light harvesting ability as well as less aggregation for the unique 3D dandelion-like hierarchical structure. The growth mechanism of the 3D dandelion-like nanostructures under various preparation conditions was also discussed.

Preparation and Analysis of Photocatalytic TiO2 Sol

In-Situ Anatase Flake Crystals Prepared By Sol-Gel Method At Low Temperature

Preparation and Properties of TiO2/Bentonite Composite Photocatalytic Materials at Room Temperature

In-Suit Preparation of Cubic Anatase Tio2 Crystals and Its Photocatalysis Property on Rhodamine B

Preparation of WO<sub>x</sub>-TiO<sub>2</sub> and the Photocatalytic Activity under Visible Irradiation

Preparation and investigation of TiO2 Sol containing nanometer anatase crystalline grains

Preparation and Investigation of TiO<sub>2</sub> Sol Containing Nanometer Anatase Crystalline Grains

Controllable hydrothermal synthesis, optical and photocatalytic properties of TiO 2 nanostructures

Effect of sol concentration on photocatalytic reaction of anatase TiO2 sol

Kinetics Analysis on Photocatalytic Reaction of Anatase Tio2 Sol

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

Effect of Water Amount on the Preparation, Structure and Property of Anatase Sol

Preparation Of Tio2 Sol Containing Anatase-Rutile Mischcrystal Grains And Its Photocatalytic Activity

PREPARATION OF ANATASE TiO2 SOL AND POWDER BY SOLVOTHERMAL SYNTHESIS

Solvothermal Growth of Three-Dimensional TiO2 Nanostructures and Their Optical and Photocatalytic Properties

Preparation of Anatase-Type TiO_2 Nanoparticals from Ti (SO4)2 Solution under Hydrothermal Conditions and Its Photocatalytic Performance

Solvothermal Synthesis of Nanosized Tio2 Particles with Different Crystal Structures and Their Photocatalytic Activities

Influence of acid catalyst on crystalline microstructure and photocatalytic property of TiO2 sol

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature

Preparation and Structural Analysis of TiO2 Photocatalytic Film Modified by Triethylamine

Preparation of Tm2Ti2O7 by Sol-Gel Method and Its Photocatalytic Activity