Abstract:In this work, TiO2 nanoparticles with exposed (001) facets, mixed-phase and particle size as small as similar to 20 nm were prepared via solvothermal process by using mixture of water and acetic anhydride as solvent and HF as shape directing agent. The as prepared TiO2 was characterized by X-ray diffraction (XRD), electron microscopes, elemental analysis (EA) and X-ray fluorescence (XRF), thermalgravimetric analysis and differential scanning calorimetry (TG-DSC), and nitrogen adsorption/desorption isotherms. The results indicated that the uncalcined sample which obtained after solvothermal process contained amorphous carbon, TiOF2, H2Ti2O5 center dot H2O, and Ti-containing organometallic compound. When calcined at temperature lower than 750 degrees C, a mixture of anatase and rutile was obtained. The photocatalytic activity of as prepared TiO2 was tested as H-2 evolution rate from water containing methanol as sacrificial agent. The photocatalytic activity for TiO2 prepared by using H2O/Ac2O as solvent was about 6 times higher than that of sample prepared by using HAc as solvent. The H-2 evolution rate over TiO2 sample prepared under optimum condition was 7.65 mmol.g(-1).h(-1), which was almost 50% higher than that of commercial P25. The influence of solvent, solvothermal temperature and calcination temperature on the morphology, particle size, phase composition and photocatalytic activity of as-synthesized TiO2 was discussed in detail. (C) 2017 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.

Solvothermal Synthesis of Nanosized Tio2 Particles with Different Crystal Structures and Their Photocatalytic Activities

Controllable Hydrothermal Synthesis, Optical and Photocatalytic Properties of TiO2 Nanostructures

Preparation and Photocatalytic Activities of TiO2 Nanotubes with Mixed Crystal Structure

Solvothermal-induced Phase Transition and Visible Photocatalytic Activity of Nitrogen-Doped Titania.

Solvothermal Growth of Three-Dimensional TiO2 Nanostructures and Their Optical and Photocatalytic Properties

Solvothermal Preparation of Tio2/Montmorillonite and Photocatalytic Activity

Preparation and investigation of TiO2 Sol containing nanometer anatase crystalline grains

Photocatalytic activity of TiO2 prepared by different solvents through a solvothermal approach

Solvothermal Synthesis of TiO2 with Exposed (001) Facets, Mixed-Phase and Small Particle Size by Using Mixture of Water and Acetic Anhydride As Solvent

Preparation of NanoTiO2 Photocatalyst Sol

Sol-Gel Preparation and Characterization of High Activity Titanium Dioxide Nanocrystalline Photocatalyst

Synthesis of Nanocrystalline Anatase TiO2 by One-Pot Two-Phase Separated Hydrolysis-Solvothermal Processes and Its High Activity for Photocatalytic Degradation of Rhodamine B.

Microemulsion-mediated solvothermal synthesis and photocatalytic properties of crystalline titania with controllable phases of anatase and rutile.

Preparation of Controllable Crystalline Titania and Study on the Photocatalytic Properties.

Characterization of Mesoporous Nanocrystalline TiO2 Photocatalysts Synthesized Via a Sol-Solvothermal Process at a Low Temperature

Hydrothermal synthesis of nano-sized titania and its photocatalytic activity

Tailored preparation of titania with controllable phases of anatase and brookite by an alkalescent hydrothermal route

Preparation and Investigation of TiO<sub>2</sub> Sol Containing Nanometer Anatase Crystalline Grains

Facile Synthesis and Active Photocatalysis of Mesoporous and Microporous Tio2 Nanoparticles

Solvothermally controllable synthesis of anatase TiO2 nanocrystals with dominant {001} facets and enhanced photocatalytic activity

Comparative Sol–Hydro(Solvo)thermal Synthesis of TiO2 Nanocrystals