Abstract:TiO2 nanocrystallines with a size of 3–7 nm have been synthesized by the sol–gel method with excessive water at a low temperature of about 50°C. The effects of amount of water and pH on the formation of sols and powders containing TiO2 nanocrystallines were investigated by X‐ray powder diffraction (XRD), transmission electron microscopy, and high‐resolution transmission electron microscopy. The results showed that a pure anatase phase was formed at pH 1, in contrast to the formation of particles with a mixture of anatase and brookite phases at pH 2–7. Moreover, at pH 1, the intensity of the XRD peaks and the crystal size increased with increasing water content when the water ratio increased from 40 to 100. Whereas the crystal intensity remained invariant, the crystal size still increased when the water ratio increased from 100 to 400. The photocatalytic activity was also investigated. It was shown that when the water ratio was below 100, the photocatalytic activity increased with increasing water content. Further increase of the water content decreased the photocatalytic activity. The photocatalytic activity decreased with increasing pH. All samples with pH=1 showed better photocatalytic activity than Degussa P25. Mechanisms for the formation of the TiO2 nanocrystalline particles at such a low temperature were also discussed.

Effect of sol concentration on photocatalytic reaction of anatase TiO2 sol

Kinetics Analysis on Photocatalytic Reaction of Anatase Tio2 Sol

In-Suit Preparation of Cubic Anatase Tio2 Crystals and Its Photocatalysis Property on Rhodamine B

Effect of Water Amount on the Preparation, Structure and Property of Anatase Sol

Preparation and Analysis of Photocatalytic TiO2 Sol

In-Situ Anatase Flake Crystals Prepared By Sol-Gel Method At Low Temperature

Preparation and Properties of TiO2/Bentonite Composite Photocatalytic Materials at Room Temperature

Preparation and investigation of TiO2 Sol containing nanometer anatase crystalline grains

Influence Of Crystallization Of Nano Tio2 Prepared By Adsorption Phase Synthesis On Photodegradation Of Gaseous Toluene

Influence of acid catalyst on crystalline microstructure and photocatalytic property of TiO2 sol

Preparation and Investigation of TiO<sub>2</sub> Sol Containing Nanometer Anatase Crystalline Grains

Photo Degradation on Rhodamine B for Anatase Tio2 Sol under Uv, Visible Light and Ir

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature

Solar photocatalytic degradation of dye wastewater in the presence of heat‐treated anatase TiO<sub>2</sub>powder

Solvothermal Synthesis of Nanosized Tio2 Particles with Different Crystal Structures and Their Photocatalytic Activities

FINE STRUCTURE OF TITANIA SOL AND ITS PHOTOCATALYTIC ACTIVITY

Research on nanometer crystal anatase TiO2 sol excitated by broad range light spectrum

Photocatalytic Degradation of Rhodamine B on Co-doped TiO_2 Thin Film under Visible Light

Synergistic Photosensitized Removal of Cr(VI) and Rhodamine B Dye on Amorphous TiO2 under Visible Light Irradiation.

Microstructure and photocatalysis kinetics of calcination-free TiO2 film

Effect of Calcination Temperature on Crystal Structure and Photocatalytic Prop- Erty of TiO2/Diatomite Nanoparticles