Abstract:Natural porous mineral supported (TiO2/diatomite) photocatalyst was prepared via a modified sol–gel method using titanium (IV) butoxide (TBOT) and diatomite. The effect of TBOT dosage on adsorption capacity and photocatalytic activity for Rhodamine B (RhB) solution was investigated. The morphology and elemental distribution were determined by scanning electron microscopy with attached energy-dispersive X-ray detector. The porous and crystalline structures were characterized using nitrogen adsorption–desorption and X-ray diffraction techniques, respectively. The prepared TiO2/diatomite hybrid catalyst has shown relatively even porous structure and dispersion of TiO2 over the surface. This suggests that the diatomite matrix prevented the agglomeration of TiO2 particles. Initially, the surface area and pore volume of the hybrid catalyst were increased by adding TBOT then decreased for dosages higher than 1.0ml. The crystalline size of TiO2 immobilized on diatomite matrix by sol–gel method was around 20nm. When the experiments were carried out in the absence of diatomite, this value was increased to 33.73nm. The use of diatomite also promoted an increase of the transformation temperature of the crystalline phase anatase to rutile for the TiO2. The as-prepared TiO2/diatomite composite exhibited high photocatalytic activity (96.0% for 0.5h UV-light irradiation) for the degradation of RhB from wastewater as a result of its unique porous structure and optimum TiO2 loading. In addition, it can be easily separated from suspension and possess a good durability. This hybrid material holds great promise in the engineering field for the environmental remediation.

Low-Temperature Growth of a Nitrogen-Doped Titania Nanoflower Film and Its Ability to Assist Photodegradation of Rhodamine B in Water

Photodegradation Of Rhodamine B In Water Assisted By Titania Nanorod Thin Films Subjected To Various Thermal Treatments

Low Temperature Synthesis of Few-Layer Titanate Nanobelts on Ti Mesh and the Hot-Water Induced Transformations to Highly Photocatalytic Active Titania Nanorods

Enhanced Ability of Nanostructured Titania Film to Assist Photodegradation of Rhodamine B in Water Through Natural Aging

Fabrication of titania thin film with composite nanostructure and its ability to photodegrade rhodamine B in water

Low‐Temperature Transformation of Titania Thin Films from Amorphous Nanowires to Crystallized Nanoflowers for Heterogeneous Photocatalysis

Photocatalytic degradation of selected dyes by titania thin films with various nanostructures

Photodegradation of Rhodamine B in Water Assisted by Titania Films Prepared Through a Novel Procedure

A Comparative Study on Photocatalytic Activity of Titania Nanowires Subjected to High-Temperature Calcination and Low-Temperature HCl Treatment

Photocatalytic Active Titania Nanowire Arrays on Ti Substrates

Construction of Ni-doped Belt-on-belt TiO2 Thin Film to Assist Photodegradation of Rhodamine B in Water

Low-Temperature Deposition of Anatase Thin Films on Titanium Substrates and Their Abilities to Photodegrade Rhodamine B in Water

Titania Nanoflowers with High Photocatalytic Activity

Photoelectrocatalytic Efficiency of Low-Temperature Precipitated Monolayer Rutile TiO 2 Nanoflower Film

Low‐Temperature Growth of Rutile Nanorod Thin Films and Their Photon‐Induced Property

Natural ageing of nanostructured titania photocatalyst films

Single-crystalline Rutile TiO2 Nanorod Array on Flexible Ti Substrates for Efficient Photoelectrocatalytic Degradation of Phenol in Water

Titania Nanowires Growing from P25 Nuclei: Facile Synthesis and the Improved Photocatalytic Activity

Large-Scale Preparation Of Ordered Titania Nanorods With Enhanced Photocatalytic Activity

Photocatalytic activity of TiO 2 nanorods, nanowires and nanoflowers filled with TiO 2 nanoparticles

Synthesis of Natural Porous Minerals Supported Tio2 Nanoparticles and Their Photocatalytic Performance Towards Rhodamine B Degradation