Abstract:A composite titania thin film consisted of quasi-aligned single-crystalline rutile nanorods embedded in sol-gel-derived anatase aggregates was fabricated and its photoelectrochemical behavior was studied in detail. A monolayer of nearly sing I e-crystal line rutile nanorods was first deposited on metallic Ti substrates through a controlled reaction between Ti and hydrogen peroxide. The gaps among the rutile nanorods were then filled with titania nanoparticles through a sol-gel dip-coating approach, which achieved a composite thin film of single-crystalline rutile nanorods embedded in anatase aggregates, after a subsequent thermal treatment at 723 K. The X-ray diffraction measurement revealed that the composite film with thickness of 180 nm contained anatase and rutile in a nearly 50:50 ratio. The UV-visible diffusive reflectance spectra estimated a band gap of 2.99 eV for the rutile monolayer and a slightly increased value of 3.03 eV for the composite film due to the embedding of the anatase nanoparticles. Photocurrent versus potential diagrams, photocurrent transient curves, and open-circuit potential measurement supported the fact that the anatase nanoparticles possessed better inherent photoelectrochemical properties than rutile. However, electrochemical impedance spectra characterization, together with photocurrent transient curves and open-circuit potential measurement, suggests that the single-crystalline rutile nanorods exhibited a higher electron-transfer rate. The combination of the two components in such an appropriate way enhanced significantly the charge separation effect arising from the anatase/rutile couple, which hence combined efficiently the "mixed crystal effect" and the "mixed morphological effect". A steady-state photocurrent more than double the simple sum of those generated by the two components alone was detected for the current composite film, which can be attributed to the single-crystalline rutile nanorods that provide channels for rapid electron transfer to the conductive Ti substrates under an applied bias potential. As a result, this study concludes that the present nanostructure magnified significantly the well-established mixed crystal effect, that is, an enhanced charge separation arising from a mixture of anatase and rutile.

Photoelectrocatalytic Efficiency of Low-Temperature Precipitated Monolayer Rutile TiO 2 Nanoflower Film

Low Temperature Synthesis of Few-Layer Titanate Nanobelts on Ti Mesh and the Hot-Water Induced Transformations to Highly Photocatalytic Active Titania Nanorods

Effects of Hydrothermal Time on the Morphologies of Rutile TiO2 Hierarchical Nanoarrays and Their Optical and Photocatalytic Properties

Low-Temperature Growth of a Nitrogen-Doped Titania Nanoflower Film and Its Ability to Assist Photodegradation of Rhodamine B in Water

Single-crystalline Rutile TiO2 Nanorod Array on Flexible Ti Substrates for Efficient Photoelectrocatalytic Degradation of Phenol in Water

Enhanced Photoelectrochemical Response of a Composite Titania Thin Film with Single-Crystalline Rutile Nanorods Embedded in Anatase Aggregates

Low‐Temperature Transformation of Titania Thin Films from Amorphous Nanowires to Crystallized Nanoflowers for Heterogeneous Photocatalysis

Low‐Temperature Growth of Rutile Nanorod Thin Films and Their Photon‐Induced Property

Titania Nanoflowers with High Photocatalytic Activity

Facile Synthesis of Ni-doped TiO2ultrathin Nanobelt Arrays with Enhanced Photocatalytic Performance

Hollow TiO 2 microspheres assembled with rutile mesocrystals: Low-temperature one-pot synthesis and the photocatalytic performance

Low‐Temperature Growth of Monolayer Rutile TiO2 Nanorod Films

Ni-doped Rutile TiO2 Nanoflowers: Low-Temperature Solution Synthesis and Enhanced Photocatalytic Efficiency

A Comparative Study on Photocatalytic Activity of Titania Nanowires Subjected to High-Temperature Calcination and Low-Temperature HCl Treatment

Photocatalytic Active Titania Nanowire Arrays on Ti Substrates

Highly Enhanced Photoelectrocatalytic Properties by Α-Fe 2 O 3 Modified NF-TiO 2 Pyramids with Dominant (101) Facets

Ordered Mesoporous Thin Films Of Rutile Tio2 Nanocrystals Mixed With Amorphous Ta2o5

Fabrication of titania thin film with composite nanostructure and its ability to photodegrade rhodamine B in water

A facile synthesis of hierarchical TiO2 for dye adsorption and photocatalysis

Activation of Carbon Cloth and Concurrent Precipitation of Titania Nanowires for Enhanced Adsorption and Photocatalysis Performance

Enhanced photoelectrocatalysis in porous single crystalline rutile titanium dioxide electrodes