Abstract:TiO2-diatomite photocatalysts were prepared by sol-gel process with various pre-modified diatomite. In order to obtain diatomite with different surface characteristics, two modification approaches including calcination and phosphoric acid treatment on the micro-structure of diatomite are introduced. The photocatalysts were characterized by XRD, XPS, nitrogen adsorption-desorption isotherms and micromorphology analysis. The results indicate that, compared with pure TiO2, the anatase-to-rutile phase transition temperature of TiO2 loaded on diatomite carrier is significantly increased to nearly 900 degrees C, depending on the different pretreatment method of diatomite. The photocatalytic activities of different samples were evaluated by their degradation rate of methyl orange ( MO) dye under UV and visible-light irradiation. The samples prepared by phosphoric acid pretreatment method exhibit the highest photocatalytic activity. After 90 min of UV irradiation, about 90% of MO is decomposed by the best effective photocatalyst. And after 8 h visible-light irradiation, nearly 60% of MO is decomposed by the same sample. Further mechanism investigation reveals that the H3PO4 pretreatment process can obviously change the surface features of diatomite carrier, cause the formation of Si-O-Ti bond, increase the binding strength between TiO2 and diatomite, restrain crystal growth of loaded TiO2, and thus form thermal-stable meso-porous structure at the granular spaces. It helps to build micro-, meso- and macro-porous hierarchical porous structure in TiO2-diatomite, and improves the charge and mass transfer efficiency during catalyzing process, resulting in the significantly increased photocatalytic activity of TiO2-diatomite pretreated by phosphoric acid. (C) 2014 Elsevier B. V. All rights reserved.

Highly Photocatalytic TiO 2 Interconnected Porous Powder Fabricated by Sponge-Templated Atomic Layer Deposition

Controllable Hydrothermal Synthesis, Optical and Photocatalytic Properties of TiO2 Nanostructures

Interface Actions Between TiO2 and Porous Diatomite on the Structure and Photocatalytic Activity of TiO2-diatomite

Fabrication and Photocatalytic Activity of Tio2 Nanofiber Membrane

A facile synthesis of hierarchical TiO<sub>2</sub>for dye adsorption and photocatalysis

Self-assembly and Photocatalysis of Mesoporous TiO 2 Nanocrystal Clusters

Sheet-on-belt Branched TiO2(B)/rGO Powders with Enhanced Photocatalytic Activity

Controllable Fabrication of TiO(2) 1D-Nano/micro Structures: Solid, Hollow, and Tube-in-tube Fibers by Electrospinning and the Photocatalytic Performance.

Fabrication and Photocatalysis of TiO2 Flower-like Nanostructures

Three-dimensional Interconnected Mesoporous Anatase TiO2 Exhibiting Unique Photocatalytic Performances

Templated Synthesis of TiO2 Nanotube Macrostructures and Their Photocatalytic Properties

Formation of hollow porous TiO2 nanospheres via the encapsulation of CO2 nanobubbles for high-performance adsorption and photocatalysis

Fabrication of Oxygen-Deficient TiO 2 Coatings with Nano-Fiber Morphology for Visible-Light Photocatalysis

Synthesis of sponge-like TiO2 with surface-phase junctions for enhanced visible-light photocatalytic performance

Ligand‐Assisted Assembly Approach to Synthesize Large‐Pore Ordered Mesoporous Titania with Thermally Stable and Crystalline Framework

Mesoporous titanium dioxide (TiO2) with hierarchically 3D dendrimeric architectures: formation mechanism and highly enhanced photocatalytic activity.

Pore structure regulation of hierarchically porous TiO2 ceramics derived from printable foams

Fabrication and Photocatalytic Properties of Porous Crystalline Titanium Dioxide Film Co-Doped with Fe and Si by PEO

Preparation and Characterization of Hierarchically Porous Monolithic TiO2

Facile fabrication of ordered assembled TiO2/g-C3N4 nanosheets with enhanced photocatalytic activity

Atomic Layer Deposition of TiO2-nanomembrane-based Photocatalysts with Enhanced Performance