Abstract:Weakly-agglomerated nanocrystalline (ZrO2)(1-x)(Sc2O3)(x) ( x = 0.02 - 0.16) powders with high surface area (106 - 186 m(2) g(-1)) and uniform particle size (5.7 - 9.5 nm) were synthesized by a two-step hydrothermal process in the presence of urea, and their complex phase evolution upon calcinations over 400 - 1400 degreesC were studied by a combined utilization of X-ray diffraction, in situ high temperature X-ray diffraction, near infrared Fourier transform Raman and ultraviolet Raman spectroscopies. It was discovered that the growth of the grains comprised two stages, and the apparent activation energies, E-a1 (<800 degrees C) and E-a2 (>800 degreesC), are in the range of 5.5 - 12 kJ mol(-1) and 80 - 140 kJ mol(-1), respectively. The crystallite size, microstrain, surface area and growth activation energy of the samples showed a strong dependence on the Sc3+ doping concentration. The nanocrystalline (ZrO2)(1-x)(Sc2O3)(x) samples underwent complex phase transitions upon calcination from 800 to 1000 degreesC. Tetragonal and cubic phases have been preserved when the samples calcined below 800 degreesC as a result of crystallite size and doping effects. At elevated calcination temperature of 1000 degreesC, the compositions at x = 0.04, 0.10 and 0.14 seemed to be in the metastable phase boundaries of m + t, t + beta (Sc2Zr7O17) and beta+gamma (Sc2Zr5O13), respectively. As calcined at 1400 degreesC, the grain size was in the micrometre regime, and t --> m, c --> t", c --> beta and c --> gamma phase transitions occurred on the cooling stage for x less than or equal to 0.04, x = 0.08, 0.10 less than or equal to x less than or equal to 0.12 and x greater than or equal to 0.14, respectively, resulting in the existence of m, t, t", beta and gamma phases in turn at room temperature. Moreover, it was found that the tetragonal phase has been enriched at the surface region for the as-calcined (ZrO2)(0.94)(Sc2O3)(0.06) and (ZrO2)(0.92)(Sc2O3)(0.08) samples.

Effects of Synthetic Parameters in Pechini Method on the Formation and Properties of (zro2)0.92(sc2o3)0.08 Solid Solution

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

(Zro 2 ) 0.85 ( RE O 1.5 ) 0.15 ( RE =sc, Y) Solid Solutions Prepared Via Three Pechini-type Gel Routes: 2—sintering and Electrical Properties

Sol–gel Synthesis and Electrical Properties of (zro2)0.85(reo1.5)0.15 (RE = Sc, Y) Solid Solutions

(Zro2)(0.85)(reo1.5)(0.15) (re = Sc, Y) Solid Solutions Prepared Via Three Pechini-Type Gel Routes: 1 - Gel Formation and Calcination Behaviors

Co-Doping Effects of Y3+ and Sc3+ on the Crystal Structures, Nanoparticle Properties and Electrical Behavior of Zro2 Solid Solutions Prepared by A Mild Urea-Based Hydrothermal Method

Synthesis of Monolithic Zirconia with Macroporous Bicontinuous Structure Via Epoxide-Driven Sol–gel Process Accompanied by Phase Separation

Citrate Gel Synthesis and Characterization of (zro2)0.85(reo1.5)0.15 (RE = Y, Sc) Solid Solutions

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

Preparation of Zirconia Powders by Sol-gel Process

Synthesis and characterization of nanocrystalline PZT powders by a simple sol-gel method

Co-precipitation of nano Mg–Y/ZrO2 ternary oxide eutectic system: Effects of calcination temperature

Effects Of Calcination Temperature And Template Content On The Structure And Properties Of Mesoporous Zirconia Microspheres

Study on the process and properties of nano-sized polycrystal zirconia powders by co-precipitation in super-alkaline medium

Processing and characterization of lead zirconate titanate nanopowders by a simple water-based sol-gel method

Nano-dispersed yttria-stabilized zirconia powder: Phase, morphology, and conductivity investigation with different chelating agents via a modified sol-gel method

Effects of Zr on the Precursor Architecture and High-Temperature Nanostructure Evolution of Sioc Polymer-Derived Ceramics

Mesoporous Yttria-Zirconia Solid Solution with Improved Textural Properties Prepared Via Lauric Acid-Assisted Synthesis

Doping and Grain Size Effects in Nanocrystalline ZrO2–Sc2O3system with Complex Phase Transitions: XRD and Raman Studies

Effect of Sintering Conditions on the Microstructure and Electrochemical Properties of 6Scandia 1Ceria co-doped Zirconia (6Sc1CeZr)

Sintering Properties of Tetragonal Zirconia Nanopowder Preparation of the NaCl + KCl Binary System by the Sol–Gel–Flux Method