Abstract:Two compositions Ce0.50Zr0.39La0.04Y0.07O2−δ and Ce0.25Zr0.65La0.04Y0.06O2−δ based on ceria-zirconia solid solutions were prepared as nanopowders using a continuous hydrothermal flow synthesis reactor, followed by either freeze-drying or hotplate-drying of the slurry. Each dried nanopowder was then subjected to 10h heat-treatment at 1000°C, 1100°C or 1200°C in air (to simulate accelerated ageing). The reducibility and hydrogen consumption of the oxidised samples were measured using temperature programmed reduction (TPR) up to 1000°C. The effects of composition, drying method and heat-treatment temperature were evaluated on the TPR profiles of the materials. The powders were further investigated using a range of analytical methods including UV/Vis spectroscopy (which yielded colour data), Raman spectroscopy, powder X-ray diffraction, BET surface area measurements and X-ray photoelectron spectroscopy (XPS). Chemometric methods were used to investigate relationships between the spectroscopic and total oxygen storage capacity (OSC) data. Principal component analysis (PCA) was used to provide a simple interpretation of the effects of various synthesis and treatment parameters on Raman spectra. Principal component regression (PCR) was used to build regression models relating the Raman spectra and the temperature of hydrogen consumption peak at several set temperatures in the TPR. The total hydrogen consumption of the materials was generally high, while the drying and heat-treatment conditions appeared to have a significant effect on the final properties of the resulting powders, such as the surface area and total oxygen storage capacity.

Study on the process and properties of nano-sized polycrystal zirconia powders by co-precipitation in super-alkaline medium

PREPARATION AND PROPERTIES OF NANOMETER POLYCRYSTALS ZIRCONIA POWDER BYSUPER ALKALINE METHOD AT LOW TEMPERATURE WITH ORGANIC ADDITIVES

Preparation and Microstructure of Nanometer Tetragonal Polycrystal Zirconia Powder at Low Temperature Condition

Study on influence mechanism of surface active agent in preparing nano-sized zirconia powders by super-alkaline coprecipitation method

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

Study on a new, environmentally benign method and its feasibility of preparing nanometer zirconia powder

Co-precipitation of nano Mg–Y/ZrO2 ternary oxide eutectic system: Effects of calcination temperature

Preparation of Zirconia Powders by Sol-gel Process

The Process and Properties of Nanometer Zirconia Powder by Environmental Benign Method

Polymerizing Mechanism and Technical Factors Optimization of Nanometer Tetragonal Polycrystalline Zirconia Slurries for the Aqueous-Gel-tape-casting Process

Preparation and properties of yttria-stabilized tetragonal phase zirconia nano-ceramics by high gravity

Synthesis and Characterization of Doped Nano-Sized Ceria–zirconia Solid Solutions

Influence of dispersant contents on rheological behavior of nano-sized tetragonal polycrystals zirconia's suspensions

Preparation of spherical zirconia powder by nano-reactor of microemulsion and its densification behavior

Phase Composition Controllable Preparation of Zirconia Nanocrystals Via Solvothermal Method

Sintering Behavior and Mechanical Properties of Alumina-Coated Zirconia Ceramics

Synthesis of the superfine high-entropy zirconate nanopowders by polymerized complex method

Nano-dispersed yttria-stabilized zirconia powder: Phase, morphology, and conductivity investigation with different chelating agents via a modified sol-gel method

Preparation of Zirconia Base Solid Solution Nanopowder by Exothermal Solid-State Synthesis

From modification to mechanism: Supercritical hydrothermal synthesis of nano-zirconia

Influence of Polyelectrolyte Dispersant on Slip Preparation of Nano-Sized Tetragonal Polycrystals Zirconia for Aqueous-Gel-tape-casting Process