Abstract:ZrO2 nanocrystals were synthesised by a microwave-assisted hydrothermal method using zirconium oxychloride (ZrOCl2·8H2O), yttrium chloride (YCl3·6H2O), and liquor ammonia (NH3·H2O) as raw materials, triethanolamine (TEOA) as mineraliser, and polyethylene glycol (PEG) as dispersant. The obtained products were characterised with thermogravimetry-differential scanning calorimetry (TG-DSC), Fourier transform-infrared spectroscopy (FT-IR), X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The results show that the concentration of ZrOCl2·8H2O had little effect on the material properties, whereas the PEG molecular weight, microwave hydrothermal time and temperature, and the concentration of TEOA greatly influenced the dispersibility of the nano-sized zirconia powders. XRD and FT-IR analyses indicated that the ZrO2 nanocrystals synthesised by the microwave hydrothermal method had a tetragonal phase without any trace of monoclinic or cubic phases. The optimal parameters for preparing nano-zirconia powders with appreciable crystallinity and crystal forms included the use of PEG1000/PEG2000/PEG4000 dispersants, a microwave hydrothermal time of 30–50 min and a temperature of 200–240 °C, and a TEOA concentration of 0.3–0.5 M. Nano-ZrO2 powder prepared via our optimised microwave hydrothermal method contained mostly tetrahedral, spherically shaped, highly homogeneous, and well-dispersed 20–30 nm particles.

Preparation of Zirconia Base Solid Solution Nanopowder by Exothermal Solid-State Synthesis

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

Study on a new, environmentally benign method and its feasibility of preparing nanometer zirconia powder

Study on Mechanism of Solid State Synthesis Nanometer Zirconia Powder

Preparation of Zirconia Powders by Sol-gel Process

Preparation of Pure Zirconia Superfine Powders by Solid-state Suspension Grinding Method

Preparation of Zirconia Nanopowders in Ultrasonic Field by the Sol-Gel Method

Preparation and Microstructure of Nanometer Tetragonal Polycrystal Zirconia Powder at Low Temperature Condition

Ethanol-induced Formation of Precursor for 8 Mol% Yttria-stabilized Zirconia: Towards the Production of Well-Dispersed, Easily Sintering, and High-Conductivity Nano-Powders

Ethanol-induced formation of precursor for 8mol% Yttria-stabilized zirconia: Towards the production of well-dispersed, easily sintering, and high-conductivity nano-powders

Preparation of spherical zirconia powder by nano-reactor of microemulsion and its densification behavior

Study on the process and properties of nano-sized polycrystal zirconia powders by co-precipitation in super-alkaline medium

A Novel Method to Prepare Mesoporous Nano-Zirconia

Preparation of Nano-ZrO2 powder via a microwave-assisted hydrothermal method

Solvothermal Synthesis of Zirconia and Yttria-Stabilized Zirconia Nanocrystalline Particles

Phase Composition Controllable Preparation of Zirconia Nanocrystals Via Solvothermal Method

Solution-Based Synthesis of Ultra-Fine ZrB2 Powders and ZrB2-SiC Composite Powders

Nanocrystalline zirconia powder processing through innovative wet-chemical methods

Preparation of spherical zirconia powder in microemulsion system and its densification behavior

Combustion Synthesis Assisted Water Atomization-Solid Solution Precipitation: A New Guidance for Nano-Zta Ceramics

Synthesis of the superfine high-entropy zirconate nanopowders by polymerized complex method