Abstract:The aim of the present work was to identify the conditions for the preparation of stable zirconia slurries with high solids content for the production of aqueous gel tape casting objects with improved properties. Influences of the powder and dispersant on the rheological properties were investigated. High stable low-viscosity nanoparticles zirconia suspensions were achieved. Nanometer-sized tetragonal polycrystal zirconia powder was synthesized by a new low-temperature environment-benign method. The oxide powders were confirmed to be 3Y-TZP single phase with tetragonal structure measured by X-ray diffraction analysis. Acryl amide (AM) and N,N′-methylene bisacrylamide (MBAM) have been used as organic monomer and cross-linker of the process, respectively. NH4PAA (M=5000–8000) has been used as polyelectrolyte dispersant. The electrokinetic behavior of nanometer-sized zirconia suspensions stabilized by various dispersant contents was studied. The result indicated the dispersant concentration greatly affected the surface charge of nanometer tetragonal zirconia powder. The isoelectric point (IEP) obviously changed from 8.1 to about 4.7 because of the addition of polyelectrolyte dispersant. To acquire stable low-viscosity slurries, the influences of several parameters on rheological behavior of nanosized tetragonal zirconia suspensions were investigated. It was found that for each factor, there exists an optimum range in which low viscosity was achieved for a slurry with high solid loading. For the slurry of 77 wt.% powder concentration with about 1.0 wt.% polyelectrolyte (based on the powder), the viscosity was 350 mPa s at the shear rate of 110 s−1. The slurry at the optimum conditions met the demands of aqueous gel tape casting process.

Polymerizing Mechanism and Technical Factors Optimization of Nanometer Tetragonal Polycrystalline Zirconia Slurries for the Aqueous-Gel-tape-casting Process

Influence of Process Factors on Polymerizing Behaviors of Nano-Sized Tetragonal Polycrystals Zirconia Slurries

Rheological properties of nanometer tetragonal polycrystal zirconia slurries for aqueous gel tape casting process

Influence of Polyelectrolyte Dispersant on Slip Preparation of Nano-Sized Tetragonal Polycrystals Zirconia for Aqueous-Gel-tape-casting Process

Sintering and behavior of nanometer tetragonal polycrystalline zirconia films by aqueous gel tape casting process

Study on the process and properties of nano-sized polycrystal zirconia powders by co-precipitation in super-alkaline medium

Optimization of the Tape Casting Slurries for High-Quality Zirconia Substrates

Synthesis of Monolithic Zirconia with Macroporous Bicontinuous Structure Via Epoxide-Driven Sol–gel Process Accompanied by Phase Separation

Gel-Tape Casting of Yttria Stabilized Zirconia Thin Film

PREPARATION AND PROPERTIES OF NANOMETER POLYCRYSTALS ZIRCONIA POWDER BYSUPER ALKALINE METHOD AT LOW TEMPERATURE WITH ORGANIC ADDITIVES

Processing of Al2O3 sheets by the gel–tape-casting process

Gelcasting of ultrafine ZrO2 at room temperature

Preparation and Microstructure of Nanometer Tetragonal Polycrystal Zirconia Powder at Low Temperature Condition

Study on influence mechanism of surface active agent in preparing nano-sized zirconia powders by super-alkaline coprecipitation method

Dispersion behavior of zirconia nanocrystals and their surface functionalization with vinyl group-containing ligands.

Study on a new, environmentally benign method and its feasibility of preparing nanometer zirconia powder

Effects of Zro_2 Powder Characteristics and Organic Additives on Preparation of Tape Casting Film

Tunable Structure of Zirconia Nanoparticles by Biopolymer Gelation: Design, Synthesis and Characterization

Preparation of spherical zirconia powder by nano-reactor of microemulsion and its densification behavior

Porous Yttria‐stabilized Zirconia Ceramics Fabricated by Nonaqueous‐Based Gelcasting Process with PMMA Microsphere As Pore‐Forming Agent

Influence of dispersant contents on rheological behavior of nano-sized tetragonal polycrystals zirconia's suspensions