Abstract:The aim of the present work was to identify the conditions for the preparation of stable zirconia slurries with high solids content for the production of aqueous gel tape casting objects with improved properties. Influences of the powder and dispersant on the rheological properties were investigated. High stable low-viscosity nanoparticles zirconia suspensions were achieved. Nanometer-sized tetragonal polycrystal zirconia powder was synthesized by a new low-temperature environment-benign method. The oxide powders were confirmed to be 3Y-TZP single phase with tetragonal structure measured by X-ray diffraction analysis. Acryl amide (AM) and N,N′-methylene bisacrylamide (MBAM) have been used as organic monomer and cross-linker of the process, respectively. NH4PAA (M=5000–8000) has been used as polyelectrolyte dispersant. The electrokinetic behavior of nanometer-sized zirconia suspensions stabilized by various dispersant contents was studied. The result indicated the dispersant concentration greatly affected the surface charge of nanometer tetragonal zirconia powder. The isoelectric point (IEP) obviously changed from 8.1 to about 4.7 because of the addition of polyelectrolyte dispersant. To acquire stable low-viscosity slurries, the influences of several parameters on rheological behavior of nanosized tetragonal zirconia suspensions were investigated. It was found that for each factor, there exists an optimum range in which low viscosity was achieved for a slurry with high solid loading. For the slurry of 77 wt.% powder concentration with about 1.0 wt.% polyelectrolyte (based on the powder), the viscosity was 350 mPa s at the shear rate of 110 s−1. The slurry at the optimum conditions met the demands of aqueous gel tape casting process.

Influence of Process Factors on Polymerizing Behaviors of Nano-Sized Tetragonal Polycrystals Zirconia Slurries

Polymerizing Mechanism and Technical Factors Optimization of Nanometer Tetragonal Polycrystalline Zirconia Slurries for the Aqueous-Gel-tape-casting Process

Influence of Polyelectrolyte Dispersant on Slip Preparation of Nano-Sized Tetragonal Polycrystals Zirconia for Aqueous-Gel-tape-casting Process

Rheological properties of nanometer tetragonal polycrystal zirconia slurries for aqueous gel tape casting process

Sintering and behavior of nanometer tetragonal polycrystalline zirconia films by aqueous gel tape casting process

Effects of Pore-Forming Agent Content on the Properties of Porous 8ysz Ceramics by Tba Based Gel-Casting

Porous Yttria‐stabilized Zirconia Ceramics Fabricated by Nonaqueous‐Based Gelcasting Process with PMMA Microsphere As Pore‐Forming Agent

Gelcasting of Nano-Sized Y-Tzp

Study on the process and properties of nano-sized polycrystal zirconia powders by co-precipitation in super-alkaline medium

Influencing factors on Al2O3 instant-solidifying forming process

Dense and Cellular Zirconia Produced by Gel Casting with Agar: Preparation and High Temperature Characterization

Optimization of the Tape Casting Slurries for High-Quality Zirconia Substrates

Processing of Al2O3 sheets by the gel–tape-casting process

Study on influence mechanism of surface active agent in preparing nano-sized zirconia powders by super-alkaline coprecipitation method

High-strength porous YSZ ceramics fabricated by TBA-based gelcasting with high solid loading slurry

Mechanical Performance of Polymer-Infiltrated Zirconia Ceramics.

Forming and Sintering of Y-TZP Nanoceramics

Gelcasting of ultrafine ZrO2 at room temperature

Effect of slurry parameters on polymerization process in gelcasting

Effect of nano-TiO2 on properties of 3 mol% yttria-stabilized zirconia ceramic via layered extrusion forming

Effects of Zro_2 Powder Characteristics and Organic Additives on Preparation of Tape Casting Film