Abstract:The container materials (glass and Teflon) employed for reflux-digesting ZrO(OH)(2) gel in basic (NH4OH: pH = 11.5, NaOH and KOH: pH = 13) solutions were shown to dramatically affect the texture, crystal phase and thermal stability of the ZrO(OH)(2) and its calcined (600 similar to 800 degreesC) ZrO2 products. Digestion in the glass container (G-preparation) led to prominent enhancement of the surface area, porosity and thermal stability of ZrO(OH)(2)/ZrO2 samples. And, the crystallization temperature on the sample DTA (differential thermal analysis) curves was shifted from ca. 460 degreesC of the undigested ZrO(OH)(2) to 800 similar to 840 degreesC of the digested ones. These effects were independent of the nature of the employed bases (NH4OH, NaOH and KOH), and small tetragonal crystallites (5 similar to 7 nm) were always obtained after the calcination at 800 degreesC. In comparison, little effects were observed for the samples digested in the Teflon container (T-preparation). Elemental analysis revealed that incorporation into ZrO(OH)(2) gel of SiO2 impurity from the glass container happened during the digestion. The surface area and pore volume of the ZrO(OH)(2) and ZrO2 samples increased linearly with the amount of Si4+ -ions in the solids. The incorporated Si4+ -ions prevented the crystallization of ZrO(OH)(2) up to temperature higher than 600 degreesC, but they induced a stabilization of very small (5 similar to 7 nm) tetragonal crystallites after the calcination at 800 degreesC. This role of the Si4+ -impurity was further confirmed with authentic SiO2-containing ZrO(OH)(2) gels prepared by coprecipitation of ZrOCl2 and Si(OC2H5)(4) in the Teflon container (ZS-preparation). When there was no incorporation of Si4+ -ions (i. e. in the T-preparation), the incorporation of alkali ions from NaOH or KOH solution could result in formation of low surface area (65 similar to 70 m(2)/g) ZrO(OH)(2) crystallites (ca. 20 nm) with mixed monoclinic and tetragonal phases. But, the incorporated alkali ions showed little effect on the texture and crystal size of the calcined (600 similar to 800 degreesC) ZrO2. In addition, dehydration and dissolution-reprecipitation of ZrO(OH)(2) gel during the digestion also affected the texture and crystal size of ZrO2 but the effect was much less important than the incorporation of Si4+ -ions.

Citrate Gel Synthesis and Characterization of (zro2)0.85(reo1.5)0.15 (RE = Y, Sc) Solid Solutions

Sol–gel Synthesis and Electrical Properties of (zro2)0.85(reo1.5)0.15 (RE = Sc, Y) Solid Solutions

(Zro2)(0.85)(reo1.5)(0.15) (re = Sc, Y) Solid Solutions Prepared Via Three Pechini-Type Gel Routes: 1 - Gel Formation and Calcination Behaviors

(Zro 2 ) 0.85 ( RE O 1.5 ) 0.15 ( RE =sc, Y) Solid Solutions Prepared Via Three Pechini-type Gel Routes: 2—sintering and Electrical Properties

Effects of Synthetic Parameters in Pechini Method on the Formation and Properties of (zro2)0.92(sc2o3)0.08 Solid Solution

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

Synthesis of Monolithic Zirconia with Macroporous Bicontinuous Structure Via Epoxide-Driven Sol–gel Process Accompanied by Phase Separation

Sol-Gel Fabrication and Electrical Property of Nanocrystalline (re2o3)(0.08)(zro2)(0.92) (re = Sc, Y) Thin Films

Nanocrystalline Rare Earth Stabilized Zirconia: Solvothermal Synthesis Via Heterogeneous Nucleation-Growth Mechanism, and Electrical Properties

Preparation of Zirconia Powders by Sol-gel Process

Enhanced Thermal Stability and Oxygen Storage Capacity for CexZr1-xO2 (x = 0.4−0.6) Solid Solutions by Hydrothermally Homogenous Doping of Trivalent Rare Earths

Effects of ZrO(OH)2 Reflux-Digestion on the Preparation of ZrO2 Nanocrystals

Citric Acid Gel Method Synthesis, Characterization And Dielectric Properties Of Single-Phase Bati4o9

Unusual Calcination Temperature Dependent Tetragonal–monoclinic Transitions in Rare Earth-Doped Zirconia Nanocrystals

Synthesis and Characterization of LixZryOz Compounds

Yttria-stabilized zirconia (8YSZ) synthesis in a supercritical CO 2 -assisted process: a parametric study for achieving cubic phase stability

Preparation, crystal structure and electrorheological performance of nano-sized particle materials containing ZrO2

Improved thermal properties and CMAS corrosion resistance of high-entropy RE zirconates by tuning fluorite-pyrochlore structure

Synthesis of nanocrystalline Ce0.8Sm0.2O 1.9 by citrate gel method

Co-precipitation of nano Mg–Y/ZrO2 ternary oxide eutectic system: Effects of calcination temperature

Nano-dispersed yttria-stabilized zirconia powder: Phase, morphology, and conductivity investigation with different chelating agents via a modified sol-gel method