Effects of ZrO(OH)2 Reflux-Digestion on the Preparation of ZrO2 Nanocrystals

SF Yin,L Li,HX Wang,BQ Xu

DOI: https://doi.org/10.3321/j.issn:0567-7351.2003.06.012

2003-01-01

Abstract:The container materials (glass and Teflon) employed for reflux-digesting ZrO(OH)(2) gel in basic (NH4OH: pH = 11.5, NaOH and KOH: pH = 13) solutions were shown to dramatically affect the texture, crystal phase and thermal stability of the ZrO(OH)(2) and its calcined (600 similar to 800 degreesC) ZrO2 products. Digestion in the glass container (G-preparation) led to prominent enhancement of the surface area, porosity and thermal stability of ZrO(OH)(2)/ZrO2 samples. And, the crystallization temperature on the sample DTA (differential thermal analysis) curves was shifted from ca. 460 degreesC of the undigested ZrO(OH)(2) to 800 similar to 840 degreesC of the digested ones. These effects were independent of the nature of the employed bases (NH4OH, NaOH and KOH), and small tetragonal crystallites (5 similar to 7 nm) were always obtained after the calcination at 800 degreesC. In comparison, little effects were observed for the samples digested in the Teflon container (T-preparation). Elemental analysis revealed that incorporation into ZrO(OH)(2) gel of SiO2 impurity from the glass container happened during the digestion. The surface area and pore volume of the ZrO(OH)(2) and ZrO2 samples increased linearly with the amount of Si4+ -ions in the solids. The incorporated Si4+ -ions prevented the crystallization of ZrO(OH)(2) up to temperature higher than 600 degreesC, but they induced a stabilization of very small (5 similar to 7 nm) tetragonal crystallites after the calcination at 800 degreesC. This role of the Si4+ -impurity was further confirmed with authentic SiO2-containing ZrO(OH)(2) gels prepared by coprecipitation of ZrOCl2 and Si(OC2H5)(4) in the Teflon container (ZS-preparation). When there was no incorporation of Si4+ -ions (i. e. in the T-preparation), the incorporation of alkali ions from NaOH or KOH solution could result in formation of low surface area (65 similar to 70 m(2)/g) ZrO(OH)(2) crystallites (ca. 20 nm) with mixed monoclinic and tetragonal phases. But, the incorporated alkali ions showed little effect on the texture and crystal size of the calcined (600 similar to 800 degreesC) ZrO2. In addition, dehydration and dissolution-reprecipitation of ZrO(OH)(2) gel during the digestion also affected the texture and crystal size of ZrO2 but the effect was much less important than the incorporation of Si4+ -ions.