Abstract:The oxalate co-precipitation method was employed to synthesize nanocrystalline Ba0.4Sr0.6TiO3 having an average particle size of 100 nm. The conventional sintering (CS) and spark plasma sintering (SPS) methods were used to fabricate Ba0.4Sr0.6TiO3 ceramics with different microstructures. The SPS sample presented uniformly dense microstructure and ultrafine grains, while abnormal grain growth and some pores were discerned in the CS sample. The differences in microstructure significantly affected the dielectric properties and energy storage performance of the ceramics. The dielectric constant of the SPS sample was high (epsilon' (similar to)1200), its dielectric loss was low (tan delta (similar to)0.003), and the sample presented diffuse phase transition and high breakdown strength (E-b = 260 kV/cm) at room temperature. Compared with the CS sample, the maximum energy storage density and energy storage efficiency of the SPS sample were increased from 0.61 to 1.20 J/cm(3) and 72.6% to 91.6%, respectively. All results revealed that SPS is a powerful technique to produce dense ceramics with high energy storage performance.

Citric Acid Gel Method Synthesis, Characterization And Dielectric Properties Of Single-Phase Bati4o9

Characterization And Dielectric Properties Of Single-Phase Ba2ti9o20 Prepared By Citric Acid Gel Method

PREPARATION AND SINTERING PROPERTIES OF BaTi4O9 BY CITRIC ACID GEL METHOD

Synthesis of BaTi2O5 Nanopowders by Sol–Gel Method and the Dielectric Properties of the Ceramics

Structure and Electrical Properties of BaTiO3 Prepared by Sol–gel Process

Synthesis of Nanocrystalline 0.94Bi(0.5)na(0.5)tio(3)-0.06Batio(3) Powder by A Citrate Method

Synthesis of Nanocrystalline 0.94Bi<sub>0.5</sub>Na<sub>0.5</sub>TiO<sub>3</sub>-0.06BaTiO<sub>3</sub> Powder by a Citrate Method

Preparation and Characterization of Nano-Crystalline Ba3Ti4Nb4O21 Microwave Dielectric Ceramic Powder

Preparation of Ba2Ti9O20 by gel self-propagation process

Improved Energy Storage Performance of Ba0.4Sr0.6TiO3 Nanocrystalline Ceramics Prepared by Using Oxalate Co-Precipitation and Spark Plasma Sintering

A Study on CSC-derived Ba 2 Ti 9 O 20 Phase Formation and Its Dielectric Property

Morphology Evolution of BaTi5O11 Nanocrystals Prepared by Hydrothermal Method and Their Permittivity

Preparation of Ti Doped BaFe12O19 Ceramics by a Sol-Gel Process

Preparation of Single-Crystalline BaTi5O11 Nanocrystals by Hydrothermal Method

Dielectric Properties of BaTiO3 Based Ceramics Prepared from Nano-powders

Preparation and Characterization of Citrate Sol-Gel Derived Ba(Zr,Ti)O3 Ceramics with Al2O3 Addition

Synthesis and Properties of Barium Titanate Based X7R Ceramics by Chemical Method

Citrate Solution Combustion Derived Ba2Ti9O20 Ceramics

Synthesis of (bi0.5na0.5)tio3 Nanocrystalline Powders by Stearic Acid Gel Method

Synthesis of BaTio3 nanocrystals by stearic acid gel method

Synthesis and performance of tetragonal Ca2+ doped BaTiO3 fine powders