Abstract:Nanocrystalline pure perovskite phase bismuth sodium titanate (Bi0.5Na0.5)TiO3(BNT) powders have been prepared by a sol-gel method from the poly vinyl alcohol evaporation route. bismuth nitrate [Bi(NO3)(3)], tetra-butyl titanate [Ti(OC4H9)(4)] and sodium acetate(CH3COONa) were used as raw materials and poly vinyl alcohol(PVA) as the sol-gel forming solvent. Stoichiometric amounts of the individual raw materials were thoroughly mixed in accordance with the BNT composition to form the stock solution. The pH of the stock was adjusted to 1-3 by adding acetate. Aqueous solution of PVA[10%(w/v)] was then added to the cationic mixture with thorough stirring. The weight ratio of the cationic mixture to the PVA aqueous solution was maintained at 2:1. The resulting viscous liquid was then heated over a hot crucible up to form a fluffy dry gel. The fluffy dry gels were calcined at different temperatures and times and then cooled to room temperature naturally. The X-ray powder diffraction(XRD) patterns of the heat-treated powders were obtained using a Bruker D8 Advance X-ray diffractometer with Cu K alpha radiation and nickel filter. Scanning electron microscope (SEM) studies of the NBT powders were performed using a JSM-6700F electron microscope. Phase-pure BNT powders were obtained at 550 degrees C for 2-2.5h which is relatively lower calcination temperature than other reports. The BNT powders consists of phase-pure perovskite nanocrystals with an average size of 100-200nm.

Synthesis of (bi0.5na0.5)tio3 Nanocrystalline Powders by Stearic Acid Gel Method

Synthesis of BaTio3 nanocrystals by stearic acid gel method

Synthesis of Nanocrystalline 0.94Bi(0.5)na(0.5)tio(3)-0.06Batio(3) Powder by A Citrate Method

Synthesis and Properties of (bi<sub>0.5</sub>na<sub>0.5</sub>)tio<sub>3</sub> Powders by Hydrothermal Method

Synthesis and properties of (Bi0.5Na0.5)TiO 3 powders by hydrothermal method

Synthesis of Nanocrystalline 0.94Bi<sub>0.5</sub>Na<sub>0.5</sub>TiO<sub>3</sub>-0.06BaTiO<sub>3</sub> Powder by a Citrate Method

Synthesis and Characterization of (na0.85k0.15)0.5bi0.5tio3 Ceramics by Different Methods

Sol-Gel Synthesis and Characterization of Nanocrystalline (bi0.5na0.5)tio3 Powders from the Poly Vinyl Alcohol Evaporation Route

Citric Acid Gel Method Synthesis, Characterization And Dielectric Properties Of Single-Phase Bati4o9

Synthesis of piezoelectric nanocrystalline PZT powder by stearic acid gel method

Synthesis of 0.94 Na0.5Bi0.5TiO3 – 0.06 BaTiO3 (NBT-6BT) lead-free piezoelectric powder suitable for aerosol deposition (AD)

Sol-gel Processing and Nanoscale Characterization of (Bi0.5na0.5)tio3-Srtio3 Lead-Free Piezoelectric Thin Films

PREPARATION AND SINTERING PROPERTIES OF BaTi4O9 BY CITRIC ACID GEL METHOD

Preparation of (NaBi)(1/2)TiO3 piezoelectric ceramic powder by sol-gel process

Preparation for BaTiO3 Nano-crystalline Powder and Study on the Sintering Characteristics of Ceramic

Preparation and Dielectric Properties of (ca0.61,nd0.26)tio3 Nanoparticles by a Sol–gel Method

Preparation and electric properties of Bi0.5Na 0.5TiO3-Bi(Al0.5Ga0.5)O3 lead-free piezoceramics

Low-temperature Preparation of Pure BaTiO_(3) by SAG Method

Preparation and Characterization of Nanocrystalline (1−x)bisco3–xpbtio3 Powder

Preparation and electric properties of Bi0.5 Na0.5 TiO3- Bi (Mg0.5 Ti0.5) O3 lead-free piezoceramics

Study on peculiar properties of nanocrystalline BaTiO3 powder and ceramics