Abstract:Nanocrystalline pure perovskite phase bismuth sodium titanate (Bi0.5Na0.5)TiO3(BNT) powders have been prepared by a sol-gel method from the poly vinyl alcohol evaporation route. bismuth nitrate [Bi(NO3)(3)], tetra-butyl titanate [Ti(OC4H9)(4)] and sodium acetate(CH3COONa) were used as raw materials and poly vinyl alcohol(PVA) as the sol-gel forming solvent. Stoichiometric amounts of the individual raw materials were thoroughly mixed in accordance with the BNT composition to form the stock solution. The pH of the stock was adjusted to 1-3 by adding acetate. Aqueous solution of PVA[10%(w/v)] was then added to the cationic mixture with thorough stirring. The weight ratio of the cationic mixture to the PVA aqueous solution was maintained at 2:1. The resulting viscous liquid was then heated over a hot crucible up to form a fluffy dry gel. The fluffy dry gels were calcined at different temperatures and times and then cooled to room temperature naturally. The X-ray powder diffraction(XRD) patterns of the heat-treated powders were obtained using a Bruker D8 Advance X-ray diffractometer with Cu K alpha radiation and nickel filter. Scanning electron microscope (SEM) studies of the NBT powders were performed using a JSM-6700F electron microscope. Phase-pure BNT powders were obtained at 550 degrees C for 2-2.5h which is relatively lower calcination temperature than other reports. The BNT powders consists of phase-pure perovskite nanocrystals with an average size of 100-200nm.

Synthesis of Nanocrystalline 0.94Bi(0.5)na(0.5)tio(3)-0.06Batio(3) Powder by A Citrate Method

Synthesis of Nanocrystalline 0.94Bi<sub>0.5</sub>Na<sub>0.5</sub>TiO<sub>3</sub>-0.06BaTiO<sub>3</sub> Powder by a Citrate Method

Synthesis of (bi0.5na0.5)tio3 Nanocrystalline Powders by Stearic Acid Gel Method

PREPARATION AND SINTERING PROPERTIES OF BaTi4O9 BY CITRIC ACID GEL METHOD

Citric Acid Gel Method Synthesis, Characterization And Dielectric Properties Of Single-Phase Bati4o9

Preparation for BaTiO3 Nano-crystalline Powder and Study on the Sintering Characteristics of Ceramic

PREPARATION OF NANOSIZED Bi3.25 La0.75 Ti3 O12 POWDER BY COPRECIPITATION METHOD

Low-temperature Synthesis of TiB2 Nanocrystals Using TiO2 ,LiBH4 and Mg

Preparation and Characterization of Nanocrystalline (1−x)bisco3–xpbtio3 Powder

Synthesis and Characterization of (na0.85k0.15)0.5bi0.5tio3 Ceramics by Different Methods

Sol-Gel Synthesis and Characterization of Nanocrystalline (bi0.5na0.5)tio3 Powders from the Poly Vinyl Alcohol Evaporation Route

Studies on the Hydrothermal Synthesis of (Bi0.5na0.5)tio3-Batio3 Powders

Low temperature preparation of nanocrystalline Sr0.5Ba 0.5Nb2O6 powders using an aqueous organic gel route

Synthesis of Nanosized (1 − X )bisco 3 − X PbTiO 3 Ferroelectric Ceramic Powders

Preparation of spherical Bi3.25La0.75Ti3O12 nanocrystals by a sol-gel inverse mini-emulsion approach

Preparation and Sintering Behaviour of Nanostructured SrBi2Ta2O9ceramics

Study on BaBi4Ti4O15 nanoscaled powders prepared by sol–gel method

A Facile One-Step Route to Nanocrystalline TiB2 Powders

Preparation and Characterization of Nano-Crystalline Ba3Ti4Nb4O21 Microwave Dielectric Ceramic Powder

Synthesis of SrBi2Ta2O9 nanocrystalline powder by a modified sol-gel process using bismuth subnitrate as bismuth source

Synthesis of BaTio3 nanocrystals by stearic acid gel method