Abstract:Nanocrystalline pure perovskite phase bismuth sodium titanate (Bi0.5Na0.5)TiO3(BNT) powders have been prepared by a sol-gel method from the poly vinyl alcohol evaporation route. bismuth nitrate [Bi(NO3)(3)], tetra-butyl titanate [Ti(OC4H9)(4)] and sodium acetate(CH3COONa) were used as raw materials and poly vinyl alcohol(PVA) as the sol-gel forming solvent. Stoichiometric amounts of the individual raw materials were thoroughly mixed in accordance with the BNT composition to form the stock solution. The pH of the stock was adjusted to 1-3 by adding acetate. Aqueous solution of PVA[10%(w/v)] was then added to the cationic mixture with thorough stirring. The weight ratio of the cationic mixture to the PVA aqueous solution was maintained at 2:1. The resulting viscous liquid was then heated over a hot crucible up to form a fluffy dry gel. The fluffy dry gels were calcined at different temperatures and times and then cooled to room temperature naturally. The X-ray powder diffraction(XRD) patterns of the heat-treated powders were obtained using a Bruker D8 Advance X-ray diffractometer with Cu K alpha radiation and nickel filter. Scanning electron microscope (SEM) studies of the NBT powders were performed using a JSM-6700F electron microscope. Phase-pure BNT powders were obtained at 550 degrees C for 2-2.5h which is relatively lower calcination temperature than other reports. The BNT powders consists of phase-pure perovskite nanocrystals with an average size of 100-200nm.

PREPARATION OF NANOSIZED Bi3.25 La0.75 Ti3 O12 POWDER BY COPRECIPITATION METHOD

The Low Temperature Synthesis and Characterization of Bi3.25la0.75ti3o12 Powder by Hydroxide Coprecipitation in Aqueous Medium

Synthesis And Characterization Of Bi3.25la0.75ti4o12 (Blt) Powders By A Two-Stage Precipitation Route

Sol–gel Synthesis and Sintering of Nano-Size Li2TiO3 Powder

Hydrothermally synthesized Pb0.70La0.30TiO3 powders

LOW-TEMPERATURE PREPARATION OF NANO-CRYSTALLINE LITHIUM NIOBATE POWDERS BY THE POLYMERIC PRECURSOR METHOD

Effect of La-Introduced Manner on the Phase Formation and Morphology of the Hydrothermally Synthesized Pb_(0.70)La_(0.30)TiO_3 Powders

Synthesis of Nanocrystalline 0.94Bi<sub>0.5</sub>Na<sub>0.5</sub>TiO<sub>3</sub>-0.06BaTiO<sub>3</sub> Powder by a Citrate Method

PREPARATION AND SINTERING PROPERTIES OF BaTi4O9 BY CITRIC ACID GEL METHOD

Preparation of spherical Bi3.25La0.75Ti3O12 nanocrystals by a sol-gel inverse mini-emulsion approach

Sol-Gel Synthesis and Characterization of Nanocrystalline (bi0.5na0.5)tio3 Powders from the Poly Vinyl Alcohol Evaporation Route

A Study on the Influencing Factors in the Preparation of Bismuth-doped Tin Oxide Nano-powders by Co-Precipitation

Synthesis of Nanocrystalline 0.94Bi(0.5)na(0.5)tio(3)-0.06Batio(3) Powder by A Citrate Method

Bi4Ti3O12 nanocrystals synthesized via hydrothermal reaction

Studies on the Hydrothermal Synthesis of (Bi0.5na0.5)tio3-Batio3 Powders

Study on BaBi4Ti4O15 nanoscaled powders prepared by sol–gel method

Further Study of Preparation of Nanosized BaTiO_3 by Way of Coprecipitation

Room-Temperature Synthesis of BaTiO<sub>3</sub>Nanoparticles in Large Batches

Preparation of Nano-Structured BaTiO3 Thin Film by Electrophoretic Deposition and Its Characterization

Preparation of Single-Crystalline BaTi5O11 Nanocrystals by Hydrothermal Method

Preparation of Strontium Titanate Nanopowder by Chemical Coprecipitation Method with New Technique