Abstract:Abstract PbZr0.52Ti0.48O3 nanocrystals were synthesized by a hydrothermal method. The effect of NaOH concentration, reaction temperature and time on nucleation and growth of PbZr0.52Ti0.48O3 nanocrystals was investigated. As the 0.05 mol/L PbZr0.52Ti0.48O3 precursors were heated at 200 °C for 21 h with NaOH concentration of 0.5 mol/L, the tetragonal PbZr0.52Ti0.48O3 nanocrystals were formed, and the grain size was more than 20 nm. With increasing the NaOH concentration from 0.5 to 1.5 mol/L, the grain size of PbZr0.52Ti0.48O3 nanocrystals decreased. When the precursors were heated at different temperatures (140 °C to 200 °C) for 21 h with 1.0 mol/L NaOH, single-phase PbZr0.52Ti0.48O3 nanocrystals were obtained at 160 °C to 200 °C. With increasing the reaction temperature from 160 °C to 200 °C, the grains size of PbZr0.52Ti0.48O3 nanocrystals increased from 5 nm to 9 nm. When the precursors were heated at 160 °C in different reaction times from 6 h to 21 h, the evolution from amorphous to crystalline PbZr0.52Ti0.48O3 nanocrystals in correlation with the reaction time was observed. Single crystalline PbZr0.52Ti0.48O3 nanocrystals with narrow size distribution (from 5 nm to 9 nm) were synthesized by controlling the NaOH concentration, reaction temperature and time. The obtained results can find potential application in preparing PbZr0.52Ti0.48O3 thin films on flexible substrates.

Hydrothermally synthesized Pb0.70La0.30TiO3 powders

Effect of La-Introduced Manner on the Phase Formation and Morphology of the Hydrothermally Synthesized Pb_(0.70)La_(0.30)TiO_3 Powders

Effect of KOH Concentration on the Phase and Morphology of Hydrothermally Synthesized Pb0.70La0.30TiO3 Fine Powders

Hydrothermal Synthesis and Phase-, Morphology-Evolution Mechanism of Lead Titanate Nanostructures Assisted with Tetramethylammonium Hydroxide

Hydrothermal synthesis and characterization of lead titanate perovskite tetragonal microplates

Hydrothermal Synthesis and Characterization of Single-Crystal Lead Titanate Nanoflakes

Hydrothermal Synthesis and Morphology Evolution of Perovskite PbTiO<sub>3</sub> Crystals with Different Lead Sources

Hydrothermal Synthesis of Single-Crystalline Perovskite PbTiO3 Nanosheets with Dominant (001) Facets

Synthesis of Pb(Zr0.52Ti0.48)O3(PZT) Powder by A Partial Lead Oxalate Coprecipitation Method

PREPARATION OF NANOSIZED Bi3.25 La0.75 Ti3 O12 POWDER BY COPRECIPITATION METHOD

Bi4Ti3O12 nanocrystals synthesized via hydrothermal reaction

The Low Temperature Synthesis and Characterization of Bi3.25la0.75ti3o12 Powder by Hydroxide Coprecipitation in Aqueous Medium

Hydrothermal Synthesis and Dielectric Properties of Lanthanum Titanate Ceramics

Hydrothermal Synthesis of Lead Zirconate Titanate Nearly Free-Standing Nanoparticles in the Size Regime of about 4 Nm

Hydrothermal Synthesis and Photoluminescence of Pre-Perovskite Lead Titanate Nanofibers

Structural and Phonon Characteristics of PbxLa1−xTiO3 Nanocrystals Prepared by Hydrothermal Technique

Polymer-assisted Hydrothermal Synthesis of Single Crystal Pb1−xLaxTiO3 Nanorods

Synthesis and Characterization of Lanthanum Hydroxide by Hydrothermal Method

XRD and raman study of nanostructured Lanthanum-modified lead titanate materials

Synthesis of Single-Crystalline Pb(Zr0.52Ti0.48)O-3 Nanocrystals by Hydrothermal Method

Poly(vinyl Pyrrolidone)-Assisted Hydrothermal Synthesis of Pb(Zr0.52Ti0.48)O3 Nanocrystals