Abstract:Abstract PbZr0.52Ti0.48O3 nanocrystals were synthesized by a hydrothermal method. The effect of NaOH concentration, reaction temperature and time on nucleation and growth of PbZr0.52Ti0.48O3 nanocrystals was investigated. As the 0.05 mol/L PbZr0.52Ti0.48O3 precursors were heated at 200 °C for 21 h with NaOH concentration of 0.5 mol/L, the tetragonal PbZr0.52Ti0.48O3 nanocrystals were formed, and the grain size was more than 20 nm. With increasing the NaOH concentration from 0.5 to 1.5 mol/L, the grain size of PbZr0.52Ti0.48O3 nanocrystals decreased. When the precursors were heated at different temperatures (140 °C to 200 °C) for 21 h with 1.0 mol/L NaOH, single-phase PbZr0.52Ti0.48O3 nanocrystals were obtained at 160 °C to 200 °C. With increasing the reaction temperature from 160 °C to 200 °C, the grains size of PbZr0.52Ti0.48O3 nanocrystals increased from 5 nm to 9 nm. When the precursors were heated at 160 °C in different reaction times from 6 h to 21 h, the evolution from amorphous to crystalline PbZr0.52Ti0.48O3 nanocrystals in correlation with the reaction time was observed. Single crystalline PbZr0.52Ti0.48O3 nanocrystals with narrow size distribution (from 5 nm to 9 nm) were synthesized by controlling the NaOH concentration, reaction temperature and time. The obtained results can find potential application in preparing PbZr0.52Ti0.48O3 thin films on flexible substrates.

Hydrothermal Synthesis and Characterization of Single-Crystal Lead Titanate Nanoflakes

Hydrothermal Synthesis of Single-Crystalline Perovskite PbTiO3 Nanosheets with Dominant (001) Facets

Hydrothermal Synthesis and Phase-, Morphology-Evolution Mechanism of Lead Titanate Nanostructures Assisted with Tetramethylammonium Hydroxide

Hydrothermal Synthesis and Photoluminescence of Pre-Perovskite Lead Titanate Nanofibers

Hydrothermally synthesized Pb0.70La0.30TiO3 powders

Hydrothermal synthesis and characterization of lead titanate perovskite tetragonal microplates

Hydrothermal Synthesis, Characterization And Growth Mechanism Of Single Crystal Lead Titanate Pyrochlore Dendrites

Hydrothermal Synthesis of Lead Zirconate Titanate Nearly Free-Standing Nanoparticles in the Size Regime of about 4 Nm

Hydrothermal Synthesis of Single-Crystalline Tetragonal Perovskite PbTiO3 Nanosheets with Dominant (001) or (111) Facets

Polymer‐Assisted Hydrothermal Synthesis of Single‐Crystalline Tetragonal Perovskite PbZr0.52Ti0.48O3 Nanowires

Synthesis of Single-Crystalline Pb(Zr0.52Ti0.48)O-3 Nanocrystals by Hydrothermal Method

Hydrothermal Synthesis and Morphology Evolution of Perovskite PbTiO<sub>3</sub> Crystals with Different Lead Sources

Effect of La-Introduced Manner on the Phase Formation and Morphology of the Hydrothermally Synthesized Pb_(0.70)La_(0.30)TiO_3 Powders

Hydrothermal Synthesis and Formation Mechanism of the Single-Crystalline Bi4Ti3O12nanosheets with Dominant (010) Facets

Effect of KOH Concentration on the Phase and Morphology of Hydrothermally Synthesized Pb0.70La0.30TiO3 Fine Powders

Bi4Ti3O12 nanocrystals synthesized via hydrothermal reaction

Poly(vinyl Pyrrolidone)-Assisted Hydrothermal Synthesis of Pb(Zr0.52Ti0.48)O3 Nanocrystals

Preparation of Single-Crystalline BaTi5O11 Nanocrystals by Hydrothermal Method

Synthesis and Crystallization Behavior of Lead Titanate from Oxide Precursors by a Hydrothermal Route

Hydrothermal Synthesis and Characterization of PbTiO<sub>3</sub> Microrods

Glucose Modified Hydrothermal Synthesis of Perovskite Oxide Nanocrystals