Effect of La-Introduced Manner on the Phase Formation and Morphology of the Hydrothermally Synthesized Pb_(0.70)La_(0.30)TiO_3 Powders

Wei Xiao,Xu Gang,Ren Zhaohui,Han Gaorong

DOI: https://doi.org/10.3321/j.issn:1002-185X.2008.z2.191

2008-01-01

Rare Metal Materials and Engineering

Abstract:Lanthanum-modified lead titanate Pb0.70La0.30TiO3 nanocrystals were successfully synthesized by using tetrabutyl titanate((C8H9O)4Ti),lanthanum nitrate(La(NO3)3.nH2O)and lead nitrate(Pb(NO3)2)as precursors and KOH as mineralizer via hydrothermal reaction route at 200 ℃,and the phase formation and morphology of the synthesized PLT powders were investigated XRD,SAED,SEM,and TEM,which are strongly influenced by the introduced manner of the precursors.It was found when lanthanum was introduced through the coprecipitated hydrous oxide of lanthanum and titanium,which strengthened their combination favoring the incorporation of lanthanum into the lead titanate matrix,the obtained powders only comprised the cubic-phase lanthanum modified lead titanate.Using the coprecipitated hydrous oxide of lanthanum and titanium as lanthanum precursor,the PLT powders with uniform spherical shape were obtained after hydrothermal reaction at 220 ℃ for 36h,the size of particles was less than 100 nm.