Abstract:Nanocrystalline pure perovskite phase bismuth sodium titanate (Bi0.5Na0.5)TiO3(BNT) powders have been prepared by a sol-gel method from the poly vinyl alcohol evaporation route. bismuth nitrate [Bi(NO3)(3)], tetra-butyl titanate [Ti(OC4H9)(4)] and sodium acetate(CH3COONa) were used as raw materials and poly vinyl alcohol(PVA) as the sol-gel forming solvent. Stoichiometric amounts of the individual raw materials were thoroughly mixed in accordance with the BNT composition to form the stock solution. The pH of the stock was adjusted to 1-3 by adding acetate. Aqueous solution of PVA[10%(w/v)] was then added to the cationic mixture with thorough stirring. The weight ratio of the cationic mixture to the PVA aqueous solution was maintained at 2:1. The resulting viscous liquid was then heated over a hot crucible up to form a fluffy dry gel. The fluffy dry gels were calcined at different temperatures and times and then cooled to room temperature naturally. The X-ray powder diffraction(XRD) patterns of the heat-treated powders were obtained using a Bruker D8 Advance X-ray diffractometer with Cu K alpha radiation and nickel filter. Scanning electron microscope (SEM) studies of the NBT powders were performed using a JSM-6700F electron microscope. Phase-pure BNT powders were obtained at 550 degrees C for 2-2.5h which is relatively lower calcination temperature than other reports. The BNT powders consists of phase-pure perovskite nanocrystals with an average size of 100-200nm.

Synthesis And Characterization Of Bi3.25la0.75ti4o12 (Blt) Powders By A Two-Stage Precipitation Route

The Low Temperature Synthesis and Characterization of Bi3.25la0.75ti3o12 Powder by Hydroxide Coprecipitation in Aqueous Medium

PREPARATION OF NANOSIZED Bi3.25 La0.75 Ti3 O12 POWDER BY COPRECIPITATION METHOD

Hydrothermally synthesized Pb0.70La0.30TiO3 powders

Effect of La-Introduced Manner on the Phase Formation and Morphology of the Hydrothermally Synthesized Pb_(0.70)La_(0.30)TiO_3 Powders

Processing- and composition-dependent characteristics of chemical solution deposited Bi<sub>4-x</sub>La<sub>x</sub>Ti<sub>3</sub>O<sub>12</sub> thin films

Processing- and composition-dependent characteristics of chemical solution deposited Bi 4−x La x Ti 3 O 12 thin films

Studies on the Hydrothermal Synthesis of (Bi0.5na0.5)tio3-Batio3 Powders

Preparation of spherical Bi3.25La0.75Ti3O12 nanocrystals by a sol-gel inverse mini-emulsion approach

Bi4Ti3O12 nanocrystals synthesized via hydrothermal reaction

Preparation and Properties of Bi4-Xlaxti3o12 Thin Films by Chemical Solution Deposition

Synthesis and Thermal Stability of Perovskite PbZr0.52Ti0.48O3 (PZT) Powders Via Precipitation Routes

Effect of KOH Concentration on the Phase and Morphology of Hydrothermally Synthesized Pb0.70La0.30TiO3 Fine Powders

Hydrothermal Synthesis and Formation Mechanism of the Single-Crystalline Bi4Ti3O12nanosheets with Dominant (010) Facets

PREPARATION AND SINTERING PROPERTIES OF BaTi4O9 BY CITRIC ACID GEL METHOD

Sol-Gel Synthesis and Characterization of Nanocrystalline (bi0.5na0.5)tio3 Powders from the Poly Vinyl Alcohol Evaporation Route

Formation and stability of pyrochlore in sputtered SBT thin films

Synthesis of Nanocrystalline 0.94Bi<sub>0.5</sub>Na<sub>0.5</sub>TiO<sub>3</sub>-0.06BaTiO<sub>3</sub> Powder by a Citrate Method

Synthesis of Pb(Zr0.52Ti0.48)O3(PZT) Powder by A Partial Lead Oxalate Coprecipitation Method

Synthesis of Nanocrystalline 0.94Bi(0.5)na(0.5)tio(3)-0.06Batio(3) Powder by A Citrate Method

Ferroelectric Properties of Bi3.25La0.75Ti3O12 Thin Films Prepared by Chemical Solution Deposition