Abstract:Nanocrystalline pure perovskite phase bismuth sodium titanate (Bi0.5Na0.5)TiO3(BNT) powders have been prepared by a sol-gel method from the poly vinyl alcohol evaporation route. bismuth nitrate [Bi(NO3)(3)], tetra-butyl titanate [Ti(OC4H9)(4)] and sodium acetate(CH3COONa) were used as raw materials and poly vinyl alcohol(PVA) as the sol-gel forming solvent. Stoichiometric amounts of the individual raw materials were thoroughly mixed in accordance with the BNT composition to form the stock solution. The pH of the stock was adjusted to 1-3 by adding acetate. Aqueous solution of PVA[10%(w/v)] was then added to the cationic mixture with thorough stirring. The weight ratio of the cationic mixture to the PVA aqueous solution was maintained at 2:1. The resulting viscous liquid was then heated over a hot crucible up to form a fluffy dry gel. The fluffy dry gels were calcined at different temperatures and times and then cooled to room temperature naturally. The X-ray powder diffraction(XRD) patterns of the heat-treated powders were obtained using a Bruker D8 Advance X-ray diffractometer with Cu K alpha radiation and nickel filter. Scanning electron microscope (SEM) studies of the NBT powders were performed using a JSM-6700F electron microscope. Phase-pure BNT powders were obtained at 550 degrees C for 2-2.5h which is relatively lower calcination temperature than other reports. The BNT powders consists of phase-pure perovskite nanocrystals with an average size of 100-200nm.

Preparation of (NaBi)(1/2)TiO3 piezoelectric ceramic powder by sol-gel process

Sol–gel Synthesis and Sintering of Nano-Size Li2TiO3 Powder

Properties of Na<sub>1/2</sub>Bi<sub>1/2</sub>TiO<sub>3</sub> Ceramic Prepared by Sol-Gel Method

Properties of Na<sub>1/2</sub>Bi<sub>1/2</sub>TiO<sub>3</sub> Ceramic Prepared by Sol-Gel Method

Preparation of BaBi4Ti4O15 powder by sol-gel process

Synthesis and properties of (Bi0.5Na0.5)TiO 3 powders by hydrothermal method

Preparation of 0.5pbtio_3/0.5nife_2o_4 Ceramic Composites by Sol-gel Method

Synthesis and Properties of (bi<sub>0.5</sub>na<sub>0.5</sub>)tio<sub>3</sub> Powders by Hydrothermal Method

Synthesis of (bi0.5na0.5)tio3 Nanocrystalline Powders by Stearic Acid Gel Method

Preparation and Dielectric Properties of (ca0.61,nd0.26)tio3 Nanoparticles by a Sol–gel Method

Preparation and Characterization of Nanocrystalline (1−x)bisco3–xpbtio3 Powder

Study on BaBi4Ti4O15 nanoscaled powders prepared by sol–gel method

Facile Preparation and Performance of Novel High-Tc Xbi(ni1/2ti1/2)o3-(1-x)pb(zr1/2ti1/2)o3 Piezoceramics

Synthesis of Nanocrystalline 0.94Bi<sub>0.5</sub>Na<sub>0.5</sub>TiO<sub>3</sub>-0.06BaTiO<sub>3</sub> Powder by a Citrate Method

Preparation and Properties of CaTiO_3:Zn Nanoparticles Based on Sol-Gel Method

Sol-Gel Synthesis and Characterization of Nanocrystalline (bi0.5na0.5)tio3 Powders from the Poly Vinyl Alcohol Evaporation Route

PREPARATION AND SINTERING PROPERTIES OF BaTi4O9 BY CITRIC ACID GEL METHOD

Synthesis of 0.94 Na0.5Bi0.5TiO3 – 0.06 BaTiO3 (NBT-6BT) lead-free piezoelectric powder suitable for aerosol deposition (AD)

Structure and Electrical Properties of BaTiO3 Prepared by Sol–gel Process

Sonochemical Preparation of PbTiO3 Fine Powders

Synthesis and Characterization of (na0.85k0.15)0.5bi0.5tio3 Ceramics by Different Methods

Preparation of (NaBi)(1/2)TiO3 piezoelectric ceramic powder by sol-gel process

Sol–gel Synthesis and Sintering of Nano-Size Li2TiO3 Powder

Properties of Na<sub>1/2</sub>Bi<sub>1/2</sub>TiO<sub>3</sub> Ceramic Prepared by Sol-Gel Method

Properties of Na&lt;sub&gt;1/2&lt;/sub&gt;Bi&lt;sub&gt;1/2&lt;/sub&gt;TiO&lt;sub&gt;3&lt;/sub&gt; Ceramic Prepared by Sol-Gel Method

Preparation of BaBi4Ti4O15 powder by sol-gel process

Synthesis and properties of (Bi0.5Na0.5)TiO 3 powders by hydrothermal method

Preparation of 0.5pbtio_3/0.5nife_2o_4 Ceramic Composites by Sol-gel Method

Synthesis and Properties of (bi&lt;sub&gt;0.5&lt;/sub&gt;na&lt;sub&gt;0.5&lt;/sub&gt;)tio&lt;sub&gt;3&lt;/sub&gt; Powders by Hydrothermal Method

Synthesis of (bi0.5na0.5)tio3 Nanocrystalline Powders by Stearic Acid Gel Method

Preparation and Dielectric Properties of (ca0.61,nd0.26)tio3 Nanoparticles by a Sol–gel Method

Preparation and Characterization of Nanocrystalline (1−x)bisco3–xpbtio3 Powder

Study on BaBi4Ti4O15 nanoscaled powders prepared by sol–gel method

Facile Preparation and Performance of Novel High-Tc Xbi(ni1/2ti1/2)o3-(1-x)pb(zr1/2ti1/2)o3 Piezoceramics

Synthesis of Nanocrystalline 0.94Bi&lt;sub&gt;0.5&lt;/sub&gt;Na&lt;sub&gt;0.5&lt;/sub&gt;TiO&lt;sub&gt;3&lt;/sub&gt;-0.06BaTiO&lt;sub&gt;3&lt;/sub&gt; Powder by a Citrate Method

Preparation and Properties of CaTiO_3:Zn Nanoparticles Based on Sol-Gel Method

Sol-Gel Synthesis and Characterization of Nanocrystalline (bi0.5na0.5)tio3 Powders from the Poly Vinyl Alcohol Evaporation Route

PREPARATION AND SINTERING PROPERTIES OF BaTi4O9 BY CITRIC ACID GEL METHOD

Synthesis of 0.94 Na0.5Bi0.5TiO3 – 0.06 BaTiO3 (NBT-6BT) lead-free piezoelectric powder suitable for aerosol deposition (AD)

Structure and Electrical Properties of BaTiO3 Prepared by Sol–gel Process

Sonochemical Preparation of PbTiO3 Fine Powders

Synthesis and Characterization of (na0.85k0.15)0.5bi0.5tio3 Ceramics by Different Methods

Properties of Na<sub>1/2</sub>Bi<sub>1/2</sub>TiO<sub>3</sub> Ceramic Prepared by Sol-Gel Method

Synthesis and Properties of (bi<sub>0.5</sub>na<sub>0.5</sub>)tio<sub>3</sub> Powders by Hydrothermal Method

Synthesis of Nanocrystalline 0.94Bi<sub>0.5</sub>Na<sub>0.5</sub>TiO<sub>3</sub>-0.06BaTiO<sub>3</sub> Powder by a Citrate Method