Structure and Electrical Properties of BaTiO3 Prepared by Sol–gel Process

Wei Li,Zhijun Xu,Ruiqing Chu,Peng Fu,Jigong Hao

DOI: https://doi.org/10.1016/j.jallcom.2009.02.137

IF: 6.2

2009-01-01

Journal of Alloys and Compounds

Abstract:BaTiO3 nanopowders were synthesized from alkoxide solution precursor by sol–gel process. Attempts had been made to understand the synthesis process with the help of thermo gravimetric (TG) and differential scanning calorimetry (DSC). XRD and SEM results showed that the BaTiO3 powders calcined at 700°C for 2h were maintained in cubic phase and the average size was 25nm. The effects of the initial grain sizes of BaTiO3 powders on the phase structures, microstructures and dielectric properties of the ceramics were investigated. The results indicated that both the grain size and the relative density of the ceramics increased with the increase in sintered temperature. The permittivity at room temperature was not sensitive to the grain size.