Low-temperature Synthesis and Characterization of Complex Perovskite (ca0.61, Nd0.26)TiO3–(Nd0.55, Li0.35)TiO3 Nanopowders and Ceramics by Sol–gel Method
Qi-Long Zhang,Fei Wu,Hui Yang,Jin-Feng Li
DOI: https://doi.org/10.1016/j.jallcom.2010.08.140
IF: 6.2
2010-01-01
Journal of Alloys and Compounds
Abstract:A sol–gel process was adopted to synthesize nanopowder with composition of (1−x)(Ca0.61, Nd0.26)TiO3–x(Nd0.55, Li0.35)TiO3 which was used to prepare the dielectric ceramics. As x≤0.8, pure solid solution phase with GdFeO3-type perovskite structure could be obtained by calcining the xerogels at 500°C. At x=0.6, the particle size calculated from the transmission electron micrograph of powder was in the range of 30–50nm. Ceramics prepared by the nanoparticles at 1150°C exhibited good dielectric properties with dielectric constant (ɛr) of 93.4, a Q×f value of 7115GHz and τf value of 0ppm/°C, which have great improvement in Q×f value and decreased the sintering temperature compared with the ceramics synthesized by solid-state method. HRTEM images showed superstructure, indicating that the solid solution phase with ordering crystal structure is helpful to the dielectric properties improvement.