Abstract:(1-x)Zn2SiO4-xTiO(2) (x=0, 5, 8, 11, and 15 wt%) ceramics have been successfully prepared through a sol-gel process. The thermal gravimetry-differential thermal analysis and X-ray diffraction analysis showed that the addition of TiO2 can lower the nucleation temperature of Zn2SiO4 and enhance the sinterability of the powders synthesized. Dense ceramics with a pure phase could be achieved at a lower temperature. The pure Zn2SiO4 ceramics sintered at 1325 degrees C exhibited microwave dielectric properties: a dielectric constant (epsilon(r)) of 6.6, a quality factor Q x f of 198 400 GHz, and a temperature coefficient of resonant frequency (tau(f)) of -41.6 ppm/degrees C. The tau(f) value can be adjusted to near zero by adding an appropriate amount of TiO2. The Zn2SiO4 ceramics containing 11 wt% of TiO2 sintered at 1200 degrees C showed excellent microwave dielectric properties: an epsilon(r) value of 9.1, a Q x f value of 150 800 GHz, and a tau(f) value of -1.0 ppm/degrees C. Our results show that the sol-gel process can achieve pure phase as well as ultrafine powders, which is beneficial to optimize the performance of Zn2SiO4 ceramics. Zn2SiO4 ceramics containing 11 wt% of TiO2 are a promising candidate for microwave and millimeter-wave applications.

Synthesis of ZnTiO3 Ceramic Powders by Sol-Gel Method

Sol–gel Synthesis and Sintering of Nano-Size Li2TiO3 Powder

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

Preparation and Properties of CaTiO_3:Zn Nanoparticles Based on Sol-Gel Method

The Characterization and Preparation of Nano-Scale Fe Doping Tio2 by Sol-Gel Method (I) - the Crystallization and Thermal Decomposition Process of Fe Doping Tio2 Xerogel Powders Using Thermal Tg-Ir Spectrometry

Characterization of ZnTiO 3 powders prepared by sol-gel process

Preparation of Zirconia Powders by Sol-gel Process

Synthesis of TiO2 material by Sol-Gel method

Synthesis, formation and characterization of ZnTiO3 ceramics

Solid-phase Synthesis and Characterization of ZnO-TiO 2 System

Formation and Transformation of Cubic ZnTiO3 Powders Prepared by Sol-gel Process

Synthesis of cadmium titanate powders by a sol-gel-hydrothermal method

Low-Temperature preparation and characterization for PbTiO3 ceramics by Sol-Gel technique

Synthesis and characterization of yttria-stabilized tetragonal zirconia polycrystalline powder coated with silica layers

Microstructure and Microwave Dielectric Properties of Tio2-Doped Zn2sio4 Ceramics Synthesized Through the Sol-Gel Process

Characterization and Electrical Properties of Sol-Gel Synthesized (sr, Pb)TiO3 Powders

Synthesis and formation mechanism of ZrC–SiC–TiC ceramic powders with high-sinterability via sol-gel process and carbothermal reduction

Synthesis of Bi0.5(Na0.825K0.175)0.5 TiO3 Fine Powders by Sol-Gel Method

Preparation and Characterization of Pb(Zr0.52Ti0.48)O3 Ultrafine Powders by a Sol-Gel Combined with Combustion Process

Preparation of pure MgTiO3 powders and the effect of the ZnNb2O6-dope onto the property of MgTiO3-based ceramics

Synthesis of PZT Nano-crystalline Powder by Sol-gel Method and Structure Characterization