Synthesis, formation and characterization of ZnTiO3 ceramics

Yee-Shin Chang,Yen-Hwei Chang,In-Gann Chen,Guo-Ju Chen,Yin-Lai Chai,Te-Hua Fang,Sean Wu

DOI: https://doi.org/10.1016/j.ceramint.2004.01.002

IF: 5.532

2004-01-01

Ceramics International

Abstract:Zinc titanate (ZnTiO3) powders of perovskite structure were synthesized by conventional solid state reaction using metal oxides. Powders of ZnO and TiO2 in a molar ratio of 1:1 were mixed in a ball mill and then heated at temperatures from 700 to 1000°C for various time periods in air. The crystallization temperature of ZnTiO3 powder was ∼820°C, activation energy for crystallization was ∼327.14kJ/mol and for grain growth was ∼48.84kJ/mol. A transition point was observed when the electrical resistivity was measured versus temperature. Like some ferroelectric materials, a PTCR behavior above the transition temperature was observed with Curie temperature of ∼5°C.

materials science, ceramics