Improved Zn 0.9 Mg 0.1 Al 2 O 4 Microwave Dielectric Ceramics with High Thermal Conductivity
Yuanxun Li,Rao Fu,MingYang Gao,Minshu Chen,Rui Peng,Yongcheng Lu
DOI: https://doi.org/10.1007/s11664-021-08829-4
IF: 2.1
2021-01-01
Journal of Electronic Materials
Abstract:Zn 0.9 Mg 0.1 Al 2 O 4 + x wt.% TiO 2 (0 ≤ x ≤ 3) microwave dielectric ceramics with relatively high thermal conductivity were prepared by solid-phase reaction. The effects of TiO 2 on the crystal phase, micromorphology, microwave dielectric properties, and thermal conductivity of the Zn 0.9 Mg 0.1 Al 2 O 4 ceramics were studied. X-ray diffraction analysis, scanning electron microscopy, laser flash measurements, and network analysis were used in this study. The results showed that a small amount of nonstoichiometric compounds appeared in the Zn 0.9 Mg 0.1 Al 2 O 4 ceramics with increasing TiO 2 content. At the same time, TiO 2 doping promoted growth of crystal grains, opened the ion-exchange channels in the system, promoted the sintering reaction, and reduced the sintering temperature of the Zn 0.9 Mg 0.1 Al 2 O 4 ceramics. Moreover, addition of TiO 2 suppressed the microscopic lattice disorder and macroscopic segregation, leading to an improvement in the dielectric properties and thermal conductivity of the composite ceramics. The Zn 0.9 Mg 0.1 Al 2 O 4 + 2 wt.% TiO 2 ceramic sintered at 1500°C exhibited the best dielectric performance and thermal conductivity with a dielectric constant of 8.57, Q × f product of 18,0861 GHz, temperature coefficient of resonance frequency of −41.5 ppm/°C, and thermal conductivity of 19.67 W/(m K).