Abstract:The effects of injecting TiO2 to a Li2O–MgO–ZnO–B2O3–SiO2 (LMZBS) microwave dielectric composite on sinterability, microstructure, crystalline phase, dielectric characteristics, mechanical characteristics, and coefficient of thermal expansion (CTE) were investigated. With the increase of TiO2 content, the main crystal orientation of the samples gradually changed from Li2MgSiO4 phase, Mg3B2O6 phase, and Mg2SiO4 phase to Li5.48Mg0.74Ti7.26O18, ZnTiO3 phase, and Mg2B2O5 and the densification temperature decreased, whisker-like crystal grains gradually increased, and the porous microstructure appeared at 15% TiO2. With the increase of TiO2 content, the densification temperature of LMZBS ceramics increases, and the dielectric constant increases with the increase of densification temperature. The CTE value decreases with the increase of titanium dioxide content, and the bending strength increases first and then decreases with the increase of titanium dioxide content. The composite with 10 wt% TiO2 content sintered at 900 °C exhibits superior performance: εr\documentclass[12pt]{minimal}\usepackage{amsmath}\usepackage{wasysym}\usepackage{amsfonts}\usepackage{amssymb}\usepackage{amsbsy}\usepackage{mathrsfs}\usepackage{upgreek}\setlength{\oddsidemargin}{-69pt}\begin{document}$${\varepsilon }_{\text{r}}$$\end{document} of 7.97, Q value of 1305 (10 GHz), flexural strength of 259 MPa, CTE value of 10.2 ppm/°C, and τf\documentclass[12pt]{minimal}\usepackage{amsmath}\usepackage{wasysym}\usepackage{amsfonts}\usepackage{amssymb}\usepackage{amsbsy}\usepackage{mathrsfs}\usepackage{upgreek}\setlength{\oddsidemargin}{-69pt}\begin{document}$${\tau }_{\text{f}}$$\end{document} value of − 13 ppm/°C. The LMZBS/TiO2 composites are suitable for LTCC application with match-well Ag electrodes.

The effect of composition on Li2(Mg0.3Zn 0.7)Ti3O8-xTiO2 microwave dielectric ceramics for low temperature co-fired ceramics technology application

Effects Of Catio(3)On Microstructures And Properties Of (1-X) Znal2o4-Xmg(2) Tio4 (X=0.1) Microwave Dielectric Ceramics

Structure and Microwave Dielectric Behaviour of Low-Temperature-fired Li2Zn1−xCoxTi3O8 (x = 0–0.07) Ceramics for Low Temperature Co-Fired Ceramic Applications

Low Temperature Sintering of Li 2 (mg 0.3 Zn 0.7 )ti 3 O 8 -0.12Tio 2 Microwave Dielectric Ceramics with Controllable Grain Size

Microwave Dielectric Properties and Low-Temperature Sintering of (zn0.8mg0.2)2sio4–tio2 Ceramics with Li2O–B2O3

Effect of TiO2 on the sintering temperature and dielectric properties of Li2O–MgO–ZnO–B2O3–SiO2 ceramic composites for LTCC applications

Microwave Dielectric Properties and Low Temperature Firing of (1 − X)li2zn3ti4o12 –xli2tio3 (0.2 ≤ X ≤ 0.8) Ceramics with B2O3–CuO Addition

Microwave Dielectric Properties of the Low-Temperature-fired Li2ZnTi3O8–Li2TiO3 Ceramics for LTCC Applications

Low temperature sintering and dielectric properties of Li 2 ZnTi 3 O 8 –TiO 2 composite ceramics doped with CaO–B 2 O 3 –SiO 2 glass

Low-Temperature-Sintering Characteristic and Microwave Dielectric Properties of (zn0.7mg0.3)tio3 Ceramics with Lbsca Glass

Low Temperature Sintering of BaO–ZnO–TiO2 Ceramics for LTCC Applications

Co 2 O 3 substitution effects on the structure and microwave dielectric properties of low-firing (Zn 0.9 Mg 0.1 )TiO 3 ceramics

Low Temperature Sintering Of Low-Loss Zntio3 Microwave Dielectric Ceramics With Zn-B-Si Glass

Microwave dielectric properties of Ba3Ti4-x(Zn1/3Nb2/3)xNb4O21 for low temperature co-fired ceramics

Temperature Stability of Low-Temperature Fired (1-X) ZnTiNb2O8-xCuTiNb2O8 Microwave Dielectric Ceramics

Low-temperature Sintering and Microwave Dielectric Properties of BaO–0.15ZnO–4TiO 2 Ceramics with Li 2 O–B 2 O 3 –sio 2 Addition

Microwave Dielectric Properties and Low Temperature Sintering of Li 2 Zn(Ti 1−x Sn X ) 3 O 8 (x ≤ 0.20) Ceramics with B 2 O 3 –cuo Addition

Low-temperature sintering mechanism and microwave dielectric properties of ZnAl2O4-LMZBS composites

Microwave Dielectric Properties and Microstructure of (li<sub>2</sub>zn<sub>3−</sub><i><sub>x</sub></i>ti<sub>4−</sub><i><sub>x</sub></i>o<sub>12−3</sub><i><sub>x</sub></i>)–<i>x</i>catio<sub>3</sub> Ceramics (<i>x</i> = 0 to 0.32)

Temperature Stability of Li2TiO3‐Zn2SiO4 Microwave Dielectric Ceramics