Abstract:SrO–BaO–B2O3–SiO2 glass-ceramics with a high dielectric constant and low dielectric loss were prepared. The influence of the SiO2/BaO ratio on the sintering behavior, crystallization behavior, and properties were systematically investigated. The results showed that the increasing amount of liquid phase from increasing the SiO2/BaO ratio promoted sintering, resulting in an initial decrease in the sintering activation energy. However, the viscosity of the liquid phase continued to increase, leading to an increase in the sintering temperature and sintering activation energy when the SiO2/BaO ratio reached 0.90. As the SiO2/BaO ratio increased, the fraction of the primary phase BaSi2Al2O8 increased, and its grains grew; the minor phase SrTiO3 was suppressed, resulting in changes in the properties of the glass-ceramics. The sample with a SiO2/BaO ratio of 0.69, which was sintered at 850 °C for 10 min, showed excellent properties: a coefficient of thermal expansion (CTE) of 10.63 × 10−6 K−1 (25–500 °C), a dielectric constant (ϵr) of 16.24 (1 MHz), a dielectric loss (tanδ) of 3.39 × 10−3 (1 MHz), a flexural strength of 138.80 MPa, and a quality loss of acid corrosion of 1.06 × 10−4 g mm−2. The results indicated that the SrO–BaO–B2O3–SiO2 glass-ceramics used in this study have great potential for low-temperature co-fired ceramics applications.

Low-temperature sintering of (Zn0.8 Mg0.2)2SiO4–TiO2 ceramics

Microwave Dielectric Properties and Low-Temperature Sintering of (zn0.8mg0.2)2sio4–tio2 Ceramics with Li2O–B2O3

Low Temperature Sintering of Li 2 (mg 0.3 Zn 0.7 )ti 3 O 8 -0.12Tio 2 Microwave Dielectric Ceramics with Controllable Grain Size

The effect of composition on Li2(Mg0.3Zn 0.7)Ti3O8-xTiO2 microwave dielectric ceramics for low temperature co-fired ceramics technology application

Low‐temperature co‐fired ceramic application of SmTaO4 and YTaO4 with ZnO‐B2O3‐SiO2 additive

Low temperature sintering and dielectric properties of (Zr0.8Sn0.2)TiO4 microwave ceramics using La2O3/BaO additives

Effects Of Catio(3)On Microstructures And Properties Of (1-X) Znal2o4-Xmg(2) Tio4 (X=0.1) Microwave Dielectric Ceramics

Low-Firing and Microwave Dielectric Properties of Ba2Ti9O20 with BaO–B2O3–ZnO Glass Addition

Enhancement of structural and microwave properties of Zn2+ ion-substituted Li2MgSiO4 ceramics for LTCC applications

Sintering behavior and properties of Li2O–MgO–ZnO–B2O3–SiO2 ceramic composites for applications in low temperature co-fired ceramic (LTCC) technologies

Low-temperature sintering and phase component modulation of 0.95MgTiO3–0.05CaTiO3 microwave dielectric ceramics

Dielectric Properties of MgO-Al2O3-SiO2 Glass-Ceramic

Microwave dielectric properties of low-temperature-fired MgNb2O6 ceramics for LTCC applications

Low-Temperature Sintering and Microwave Dielectric Properties of Ba2Ti9O20 Ceramics with CaO–B2O3–ZnO Glass Additions

Low-fire Processing of Microwave (ca 1−x Sr X )(zr 1−y Mn Y )O 3 Dielectric with Li 2 O-B 2 O 3 -Sio 2 Glass in H 2 /N 2

Effects of MgO, SrO and La$lt;inf$gt;2$lt;/inf$gt;O$lt;inf$gt;3$lt;/inf$gt; Co-doping on Structure and Properties of (Zr$lt;inf$gt;0.8$lt;/inf$gt;Sn$lt;inf$gt;0.2$lt;/inf$gt;)TiO$lt;inf$gt;4$lt;/inf$gt; Ceramics

Low-temperature sintering and microwave dielectric properties of LiF-doped CaMg1−Zn Si2O6 ceramics

Low temperature sintering and microwave dielectric properties of Ba2Ti3Nb4O18 ceramics for LTCC applications

Synthesis and characterization of La2O3/BaO-doped (Zr0.8Sn0.2)TiO4 microwave ceramics

Sintering and microwave dielectric properties of LTCC-zinc titanate multilayers

Effect of SiO2/BaO ratio on sintering behavior, crystallization behavior, and properties of SrO–BaO–B2O3–SiO2 glass-ceramics