Abstract:The crystal structure of (Zn1-xCox)(0.5)Ti-0.5(Nb1-yTay)O-4 microwave dielectric ceramics was determined by Rietveld refinement. The XRD results show orthorhombic structure of Zn0.5Ti0.5NbO4 and appearance of a second phase Zn0.7Nb0.33Ti0.5O2 with tetragonal structure. The relationships between the dielectric polarizability, the second phase content, bond length, bond strength, bond valence, packing fraction and microwave dielectric properties were systematically discussed. The er values decrease at first (x = 0, 0.1) because of the decreased polarizability and a lower relative density, while after x = 0.2, a second phase is formed, which increases the epsilon(r) to a great extent. The Q x f values drop are mainly ascribed to the decrease of packing fraction, grain size and the increase of the second phase content. With the decrease of bond valence of Ti-O and oxygen octahedron distortion, the tau(f) values increase. Excellent microwave properties of the ceramics sintered at 1175 degrees C were obtained for x = 0.2 and y = 0.3: epsilon(r) = 38.02, Q x f = 23,550 GHz, tau(f) = 4.62 ppm/degrees C.Furthermore, Li2O-B2O3-SiO2 (LBS) glass was used to lower the sintering temperature. The effects of LBS glass on the crystal structure, sintering behavior and activation energy were also discussed. These results indicate that LBS glass significantly lowers the activation energy and has no influence on the phase composition. The ceramics sintered at 900 degrees C for 4 h show great properties: epsilon(r) = 34.10, Q x f = 13,349 GHz, tau(f) = 7.12 ppm/degrees C, which is promising for LTCC application. (C) 2017 Elsevier B.V. All rights reserved.

Low‐temperature co‐fired ceramic application of SmTaO4 and YTaO4 with ZnO‐B2O3‐SiO2 additive

Effects of Li2O-B2O3-SiO2 glass on the low-temperature sintering of Zn0.15Nb0.3Ti0.55O2 ceramics

Influence of Li2O–B2O3–SiO2 Glass on the Sintering Behavior and Microwave Dielectric Properties of BaO–0.15ZnO–4TiO2 Ceramics

Low-temperature sintering of (Zn0.8 Mg0.2)2SiO4–TiO2 ceramics

Low Temperature Sintering of Zn1.8sio3.8 Dielectric Ceramics Containing 3Zno-2B(2)o(3) Glass

Low-Firing Ba_4(Nd_(0.85)Bi_(0.15))_(28/3)Ti_(18)O_(54) Microwave Ceramics

Low-Firing and Microwave Dielectric Properties of Ba2Ti9O20 with BaO–B2O3–ZnO Glass Addition

A Synergistic Effect of Li-B-Si Glass and La-B on Low-Temperature Sintering of Bao-0.15zno-4tio(2) Dielectric Ceramic

Low-temperature Sintering and Microwave Dielectric Properties of BaO–0.15ZnO–4TiO 2 Ceramics with Li 2 O–B 2 O 3 –sio 2 Addition

Low Temperature Sintering Kinetics and Microwave Dielectric Properties of BaTi5O11 Ceramic

Low temperature sintering and dielectric properties of Li 2 ZnTi 3 O 8 –TiO 2 composite ceramics doped with CaO–B 2 O 3 –SiO 2 glass

Low-firing, Temperature Stable and Improved Microwave Dielectric Properties of ZnO TiO2Nb2O5 Composite Ceramics

Synthesis of Ba{[(Mg0.8Zn0.2)(0.98)Y-0.02](1/3)Tan(2/3)}O-3 Microwave Dielectric Ceramics with La2O3-B2O3-ZnO Glass for LTCC Application

Low Temperature Sintering Kinetics of BaO-0.15ZnO-4TiO2 Dielectric Ceramic in the Presence of a Liquid Phase

Structure, Microwave Properties and Low Temperature Sintering of Ta2O5 and Co2O3 Codoped Zn0.5Ti0.5NbO4 Ceramics

Low-temperature sintering mechanism and microwave dielectric properties of ZnAl2O4-LMZBS composites

Low-temperature Sintering and High-Frequency Dielectric Properties of ZTS Ceramics with V 2 O 5 –B 2 O 3 Addition

Low-firing and Temperature Stability Regulation of Tri-Rutile MgTa2O6 Microwave Dielectric Ceramics

Low Temperature Sintering Of Low-Loss Zntio3 Microwave Dielectric Ceramics With Zn-B-Si Glass

Crystal structure, Raman spectra, and modified dielectric properties of pure-phase ZnZrNb<sub>2</sub>O<sub>8</sub> ceramics at low temperature

The effect of composition on Li2(Mg0.3Zn 0.7)Ti3O8-xTiO2 microwave dielectric ceramics for low temperature co-fired ceramics technology application