Low temperature sintering and microwave dielectric properties of BaO–0.6ZnO–2.9TiO 2 ceramics using BaCu(B 2 O 5 ) addition

Sen Peng,Jianming Xu,Hao Li,Tongcheng Huang,Shaojie Wang,Bing Xie,Gaofeng Luo,Jianhua Zhou

DOI: https://doi.org/10.1007/s10854-015-3562-6

2015-01-01

Abstract:In this paper, the effect of BaCu(B 2 O 5 ) addition on the sintering process, phase composition, microstructure and microwave dielectric properties of BaO–0.6ZnO–2.9TiO 2 ceramics were investigated by the conventional solid-state reaction technique. It was suggested that the liquid phase of BaCu(B 2 O 5 ) was responsible for the densification of the BaO–0.6ZnO–2.9TiO 2 ceramics at approximate 900 °C. Using EDX analysis the evaporating of boron was confirmed and Cu 2+ most likely substituted for Zn 2+ sites in the phases Ba 4 ZnTi 11 O 27 and BaZn 2 Ti 4 O 10 . BaTiO 3 phase appearing at the grain boundary as the derivative of BaCu(B 2 O 5 ) had a considerable negative effect on the microwave dielectric properties. The variation tendency of dielectric constant was increased in accord with the trend between bulk densities and the sintering temperature. The maximum Q × f value of 15200 GHz was obtained for the specimen with 7 wt% BaCu(B 2 O 5 )The specimen with 7 wt% BaCu(B 2 O 5 ) addition sintered at 900 °C for 1.5 h showed dense microstructure and had acceptable microwave dielectric properties: dielectric constant ε r = 37, Q × f = 15200 GHz and the temperature coefficient of resonant frequency τ f = −9.8 ppm/°C.