Low Temperature Sintering and Dielectric Properties of BaTi_(0.75)Zr_(0.25)O_3 Ceramic

Su Kuifan,Chen Di,Deng Xiangyun,Li Jianbao,Wang Chunpeng,Zhang Guoqing,Wang Liming

2012-01-01

Abstract:Through adding different content B2O3,BaZr0.25Ti0.75O3(BZT) ceramics were prepared by conventional ceramic process at a relatively low sintering temperature,and the dielectric properties of the ceramics were studied.The phase of the ceramics was analyzed by X-ray diffraction.The results indicate that the main crystal phase of the BZT ceramic with B2O3 sintered at 1 150 ℃ shows perovskite structure and has no obvious additional phase.Through observing the surface morphology,it was found that the grain size of the ceramic increases gradually with the B2O3 content at 0%～1.5% and decreases slightly with the B2O3content at 1.5%～2.5%.With the increase of B2O3 content,the dielectric constant of the BZT ceramic decreases but the dielectric loss increases slightly.Compared with the pure BZT ceramic,the sintering temperature of the BZT ceramic with B2O3reduces by 300 ℃,and the structure and dielectric properties of the BZT ceramic with 1.5% B2O3show better.