Effects of Ion Diffusion and Dielectric Composite on Properties of Highly Tunable Ba2SiO4– Ba0.4Sr0.6TiO3 Composite Ceramics
Xianxin Zhang,Mingwei Zhang,Le Xin,Panpan Lyu,Luchao Ren,Zhengxin Li,Xinyuan Lyu,Zheng Luo,Jia Wang,Jiwei Zhai
DOI: https://doi.org/10.1016/j.ceramint.2022.12.198
IF: 5.532
2023-01-01
Ceramics International
Abstract:xBa2SiO4-(1-x)Ba0.4Sr0.6TiO3 (x = 10-50 wt%) composite ceramics were prepared via solid-state and liquid sintering. Ion diffusion between Ba2SiO4 (BS) and Ba0.4Sr0.6TiO3 (BST40) phases occurred in all the composites, and was enhanced during the liquid sintering process. A additionally, molten BS inhibited abnormal grain growth in BST and accelerated the densification of the composites. The increase in the Ba/Sr ratio in BST with x, owing to the A site ion diffusion, promoted an increase in the Curie temperature of the composite ceramics, with a concurrent increase in their tunability. The recombination effect maintained the Q value of the composite ce-ramics above 200, offsetting the negative effect of ion diffusion on the Q value, for x > 30 wt %. The 50 wt% BS -50 wt% BST samples exhibit a high comprehensive performance with dielectric permittivity, tunability, and Q value of 376, 32.6%, and 428, respectively.