Effects of Lithium Fluoride Additives on the Microstructure and Dielectric Properties of Barium Strontium Titanate Ceramics

Liu Shanshan,Zhao Yuzhen,Wang Xilin,Zhou Heping

2015-01-01

Rare Metal Materials and Engineering

Abstract:Lithium fluoride was employed as sintering aids to adjust the microstructure and dielectric properties of barium strontium titanate ceramics (Ba0.6Sr0.4TiO3, BSTO). The phase structure, microstructure and dielectric properties of LiF doped BSTO ceramics were studied. The XRD patterns show all samples exhibit a perovskite structure, and no secondary phased is observed. The SEM photographs indicate that the grain size is increased with the increasing of LiF additives. The dielectric constant is reduced with a small amount of LiF and increased with further increase of LiF additives, while the dielectric loss is declined significantly with a small amount of LiF. The dielectric properties are influenced strongly by LiF additives, but the Curie temperature of the samples remains the same. The K-factor is increased with the increasing of LiF additives. BSTO ceramics with 5 wt% LiF additives possess the highest performance. The room temperature dielectric constant, dielectric loss, and relative dielectric tunability at 150 kHz are 3360, 3.5 x 10(-4), and 44%, respectively.