The role of CuO addition in the phase evolution and properties of BaTi5O11 microwave dielectric ceramics prepared by the solid-state reaction method

Shupei Zhu,Ying Dai,Xinmei Pei

DOI: https://doi.org/10.1007/s10854-022-08532-y

2022-06-15

Abstract:The ceramic specimens with the nominal compositions of BaTi 5 O 11 – x CuO ( x = 0, 0.005, 0.010, 0.015, and 0.020 mol) were prepared via a solid-state reaction method. The effects of CuO addition on the phase formation, sintering, and microwave dielectric properties of BaTi 5 O 11 were investigated. The addition of CuO promoted formation of a single-phase BaTi 5 O 11 at 1050 °C and enhanced the stability of the phase at elevated temperatures up to 1150 °C. It was found for the ceramic specimens that the added Cu 2+ substituted for the Ba 2+ in the lattice of the BaTi 5 O 11 phase, causing an inclination of the TiO 6 octahedron. The Cu 2+ incorporation into the lattice served to promote the densification of the ceramic specimens. Moreover, The Cu 2+ incorporation helped to decrease the temperature coefficient of the resonant frequency of the ceramics. The BaTi 5 O 11 − 0.010 CuO ceramic sintered at 1060 °C for 4 h has good microwave dielectric properties, including a relative dielectric constant ε r = 43.6 ± 0.2, high quality factor Q × f = 35,500 ± 200 GHz (6 GHz), and temperature coefficient of resonant frequency of close to zero τ f = 1.0 ± 0.5 ppm/°C.