Structure and Microwave Dielectric Properties of Hexagonal Ba[Ti1-X(Ni1/2w1/2)(X)]O-3 Ceramics

Fei Zhao,Zhenxing Yue,Jing Pei,Hao Zhuang,Zhilun Gui,Longtu Li

DOI: https://doi.org/10.1111/j.1551-2916.2007.01801.x

IF: 4.186

2007-01-01

Journal of the American Ceramic Society

Abstract:Microwave dielectric ceramics with the composition of Ba[Ti1-x(Ni1/2W1/2)(x)]O-3 (x = 0.4-0.6) were prepared by a solid-state reaction method. The evolution of the crystalline phases was investigated by X-ray powder diffraction analysis. A cubic-to-hexagonal phase transition occurred between 1000 degrees and 1300 degrees C. The phase transition is irreversible; thus, the hexagonal phase remains stable at room temperature. The X-ray powder diffraction data for x = 0.5 were refined using the Rietveld method. It was identified as a h-BaTiO3-type hexagonal perovksite with the space group of P6(3)/mmc. It also reveals that random occupancy of Ti4+ and W6+ ions occurs in the B-site substructures, whereas Ni2+ ions exclusively occupy the octahedral site in the corner-sharing octahedron. The dielectric properties of dense-sintered ceramics were characterized at microwave frequencies. With an increase in x from 0.4 to 0.6, the Q x f value increased from 26 700 to 42 000 GHz, whereas epsilon(f), decreased from 29.8 to 20.0, and tau(f) from +6.5 to -9.9 ppm/degrees C.