Low-fire Processing of Microwave (ca 1−x Sr X )(zr 1−y Mn Y )O 3 Dielectric with Li 2 O-B 2 O 3 -Sio 2 Glass in H 2 /N 2

Yueh-Ting Shih,Jau-Ho Jean

DOI: https://doi.org/10.1016/j.ceramint.2017.05.215

IF: 5.532

2017-01-01

Ceramics International

Abstract:The effects of Li2O-B2O3-SiO2 (LBS) glass addition on densification and dielectric properties of (Ca1−xSrx)(Zr1−yMny)O3 fired in a reducing atmosphere have been investigated. The dielectric properties of (Ca1−xSrx)ZrO3 become better with decreasing the ratio of Sr/Ca. Substituting Zr by 0.2mol Mn, the dielectric loss of (Ca0.9Sr0.1)ZrO3 is greatly reduced, resulting in a Q × fr value of 30500GHz. To reduce the densification temperatures of (Ca0.9Sr0.1)(Zr0.8Mn0.2)O3 (CSZM9182) to the range cofirable with Cu electrode, 5–10vol% LBS glass is added and the densification temperature is lowered from 1500°C to 1030°C. The densification is further enhanced with increasing [B2O3]/[SiO2] ratio in the LBS glass, however, the dielectric properties are deteriorated. The above result is attributed to a chemical reaction taking place at the interface of CSZM9182-LBS during firing, which becomes more extensive with increasing [B2O3]/[SiO2] ratio in the LBS glass and tends to form a second phase of CaZr4O9. For the LBS glass with 40mol% Li2O, 20–50mol% B2O3, and 10–40mol% SiO2, the resulting CSZM9182 +5–10vol% LBS microwave ceramics have a dielectric constant of 23–27, Q × fr value of 2500–22,000GHz at 7.6–7.8GHz, and a temperature coefficient of resonant frequency (τf) of −22~ −7ppm/°C in the temperature range between 25°C and 80°C.